Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 11.3 GPa | 1640 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers UTTAP SF 50030GF Polyethersulfone, 30% Glass Reinforced Glass reinforced (30 %) Polyether Sulfone, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50%.. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers UTTAP™ SF 50030 GF Polyether Sulfone, 30% Glass Fiber Excellent chemical and electrical resistance, high stiffness, modulus and HDTAll properties after 48hrs conditioning at 23°C/50% RH |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Europe-Africa-Middle East) Thermally conductive mineral filled PA6 non-halogen FR compound |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
LNP Thermocomp® OF-1006 Polyphenylene Sulfide, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
LNP Lubricomp® EFL-4036 Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant
(discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac.. |
|||
Flexural Modulus | 11.3 GPa @Temperature 22.0 °C |
1640 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® BMC 2900 Unsaturated Polyester UP BMC 2900 is a specially designed BMC to meet the EC Safety Signs Directive (92/58/EEC) on the provision and use of safety signs at work. In areas where it is not possible to include the use of illu.. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Asia Pacific) LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP EFL36XXC PEI LNP* Lubricomp* EFL36XXC is a compound based on Polyetherimide containing 30% Glass Fiber, 155 PTFE. Characteristics of this grade are: Internally Lubricated. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing 40% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific) LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
Solvay Specialty Polymers Amodel® AS-1935 HS Polyphthalamide (PPA), 35% Glass Fiber Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e.. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® VB-5400G PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP RF008ESY PA 66 LNP THERMOCOMP* RF008ESY is a compound based on Nylon 66 resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON DX05042 PC (Europe-Africa-Middle East) LNP* Stat-kon* DX05042 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® VB-5400G PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66 Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | ASTM D790 |
Plenco 1501 Polyester, Briquette, Transfer Molded PLENCO 01501 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance properties, low post shrinkage, and improved mechanical strength va.. |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | cond; ISO 178 |
DSM EcoPaXX® Q-HG10 PA410-GF50 50% Glass Reinforced, Heat Stabilized |
|||
Flexural Modulus | 11.3 GPa | 1640 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Verton RX93407D PA 66 LNP* Verton* RX93407D is a compound based on Nylon 66 resin.This data was supplied by SABIC-IP for the Americas region. |