- Menzolit Menzolit® BMC 2900 Unsaturated Polyester UP
Menzolit Menzolit® BMC 2900 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® BMC 2900 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BMC 2900 is a specially designed BMC to meet the EC Safety Signs Directive (92/58/EEC) on the provision and use of safety signs at work. In areas where it is not possible to include the use of illuminated signs BMC 2900 moulds luminescent parts . Besides flat luminescent panels it is possible to mould three dimensional parts like safety helmets, escape way stairs or other safety and wrning items of luminescent properties . These are in addition to traditional signboards such as prohibition, warning signs as well as fire safety signs (ie signs for fire exits and fire-fighting equipment). The parts comply with DIN 67510 for safety applications.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | ISO 1183 |
| Water Absorption | 0.00 % | 0.00 % | ISO 62 |
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Flexural Strength | 50.0 MPa @Temperature 22.0 °C |
7250 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 11.3 GPa @Temperature 22.0 °C |
1640 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 170 °C | 338 °F | ISO 11357-2 |
| Oxygen Index | 42 - 43 % | 42 - 43 % | ISO 4589-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Comparative Tracking Index | 601 V | 601 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 136 - 155 °C | 277 - 311 °F | 0 moulding, matched metal die |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1205 Glass Reinforced SMC
- SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC
- Nye Lubricants 910 (NG) Synthetic Oil
- SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA
- Hexcel® HexWeb® HRH-327 - 1/8 - 3.2 Fiberglass Reinforced Polyimide Honeycomb
- EMS-Grivory Grivory® XE 4107 black 9992 PA612-GF40
- Dow Corning 1500 Antifoam
- Braskem BC818 Extrusion Coating Low Density Polyethylene
- Polykemi AB POLYfill PPHC T8020 Polypropylene, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved