SABIC Innovative Plastics LNP LUBRICOMP EFL36XXC PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP EFL36XXC PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* EFL36XXC is a compound based on Polyetherimide containing 30% Glass Fiber, 155 PTFE. Characteristics of this grade are: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
ASTM D792
1.62 g/cc
0.0585 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
50% RH, 24 hrs; ASTM D570
0.220 %
0.220 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
 0.0010 - 0.0030 in/in

@Time 24.0 hour
 ASTM D955
0.0021 - 0.0024 cm/cm

@Time 86400 sec
 0.0021 - 0.0024 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0035 - 0.0047 cm/cm

@Time 86400 sec
 0.0035 - 0.0047 in/in

@Time 24.0 hour
 ISO 294
0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 168 MPa
24400 psi
5 mm/min; ISO 527
175 MPa
25400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 11.18 GPa
1622 ksi
1 mm/min; ISO 527
12.68 GPa
1839 ksi
50 mm/min; ASTM D638
Flexural Strength 248 MPa
36000 psi
ISO 178
252 MPa
36500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 11.3 GPa
1640 ksi
1.3 mm/min, 50 mm span; ASTM D790
11.39 GPa
1652 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.22 J/cm
2.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.10 J/cm
13.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²
21.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
 7.38 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.45
0.45
ASTM D3702 Modified
Coefficient of Friction, Static 0.43
0.43
ASTM D3702 Modified
K (wear) Factor 70.5 x 10-8 mm³/N-M
35.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 39.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
39.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 21.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 27.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
28.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
399 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
202 °C

@Thickness 3.20 mm
 396 °F

@Thickness 0.126 in
 unannealed; ASTM D648