DSM EcoPaXX® Q-HG10 PA410-GF50
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | EcoPaXX® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM EcoPaXX® Q-HG10 PA410-GF50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% Glass Reinforced, Heat Stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.10 % | 1.10 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | cond; ISO 527-1/-2 |
| 220 MPa | 31900 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 3.5 % | 3.5 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 12.0 GPa | 1740 ksi | cond; ISO 527-1/-2 |
| 16.0 GPa | 2320 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 250 MPa | 36300 psi | cond; ISO 178 |
| 335 MPa | 48600 psi | dry; ISO 178 | |
| Flexural Modulus | 11.3 GPa | 1640 ksi | cond; ISO 178 |
| 14.6 GPa | 2120 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 1.90 J/cm² @Temperature 23.0 °C |
9.04 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C | 23.3 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | dry; ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Calculated Bio Based Carbon Content (%) | 70 | ASTM 6866 |
Users viewing this material also viewed the following:
- Omya OMYACARB® 6 - PT Calcium Carbonate
- Polymer Resources NY6/12-G43 Nylon 612, 43% Glass Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP RFL25ES PA 66 (Europe-Africa-Middle East)
- Saint-Gobain Chemlam® RL® RL4000 PTFE-Coated Non-woven Aramid Reinforced Laminate
- SABIC Innovative Plastics LNP Thermotuf VFM53 PA 66 (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp 9X04488 POLYPHENYLENESULFONE
- A. Schulman PP 1329H-01 Polypropylene Medium Impact Polypropylene
- Chase Plastics CP Pryme® NN113L (Dry) Nylon 66, 13% Glass Fiber Reinforced, Lubricated
- Clariant Renol BR7008 Polycarbonate/Polyester Alloy
- EMS-Grivory Grivory® BG-50 FC PA6-GF50
Copyright © lookpolymers.com All Rights Reserved