Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
PolyOne Nymax™ GF 1800 43 Black 22 Polyamide 612 (Nylon 612) Property data for molded test bars: Dry as MoldedInformation provided by PolyOne |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.. |
|||
Flexural Modulus | 10.27 GPa | 1490 ksi | ASTM D790 |
Plenco 50030 PET, Pellet, Injection Molded, Black
(discontinued **) PLENCO 50030 is an engineering grade glass reinforced polyethylene terephthalate resin designed for good physical strength. It is UL listed and available in white, natural, and black.Information sup.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
PolyOne Therma-Tech™ LC-5000C TC LCP
(discontinued **) Therma-Tech™ Thermal Management Compounds have been engineered to combine the heat transfer and cooling capabilities of metals with the design freedom, weight reduction and cost advantages of therm.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | 2 mm/min; ISO 178-A |
Lanxess Pocan® ECO T 3230 000000 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS. |
|||
Flexural Modulus | 10.27 GPa | 1490 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66 (Asia Pacific) LNP* LUBRICOMP* RX06480 is a compound based on Nylon 66 resin containing PTFE, Glass Fiber, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber Amodel® A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment... |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
Solvay Specialty Polymers KetaSpire® KT-820 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber KetaSpire® KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaS.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
Solvay Specialty Polymers Ryton® XE4050BL Polyphenylene Sulfide Alloy (PPS Alloy), GlassMineral Filled Ryton® XE4050BL glass fiber and mineral filled polyphenylene sulfide alloy compound provides high ductility and impact strength along with good thermal stability.Features: Ductile; Good Thermal S.. |
|||
Flexural Modulus | 10.27 GPa | 1490 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP KF006 Acetal Copoly LNP* THERMOCOMP* KF006 is a compound based on Acetal Copolymer resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled. |
|||
Flexural Modulus | 10.27 GPa | 1490 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF0059 PA 66 LNP THERMOCOMP* RF0059 is a compound based on Nylon 66 resin containing 25% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 LNP* THERMOCOMP* RF006S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® N602G6S Nylon 66, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC (Asia Pacific) LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 9X94104 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* 9X94104 is a compound based on Polyetherimide resin containing Glass Fiber. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® 80G43HS1L BK104 Nylon 66
(Unverified Data**) 43% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G43HS1L BK104 is a 43% glass fiber reinforced heat stabilized black polyamide 66 resin with superior impact resistance.Information.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® HTN 51G35HSLR BK420J Polyphthalamide (PPA)
(Unverified Data**) 35% Glass Reinforced PPA High Performance Polyamide with Improved Surface Appearance Zytel HTN51G35HSLR BK420J is a 35% glass reinforced heat stabilized lubricated high performance polyamide resin w.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
E-Polymers Tekaster® F615GFR , Flame Retardant, 30% Glass Reinforced PET 30% Glass Fiber Reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
Chem Polymer Chemlon 215 GVH Nylon 6, 15% Glass Fiber Reinforced A glass fiber reinforced, flame retardant nylon 6. The material has a V0 flammability rating according to UL 94 testing procedure at thicknesses down to 1/16" (1.57mm).Data provided by the manufact.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
A. Schulman ComAlloy Voloy® 417 Polyester - PBT, Glass/Mineral Reinforced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.43% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA)
(Unverified Data**) Amodel A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment. Thi.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
LATI LARAMID G/30 30% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s.. |
|||
Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 |
Rostone Rosite® 4030FS SMC Thermoset Polyester, 30% Glass Reinforced
(discontinued **) Key Features: "Zero Shrink" Grade±1/4 mil shrinkage. Provides surface smoothness for uses such as auto headlamp retainers. High impact and flexural strength combined with dimensional accuracy.Inf.. |