Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.80 GPa | 841 ksi | |
Plastcom SLOVAMID 6 GF 20 FRG 3 PA6, 20% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 20 % glass fibre, with halogen free flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 9.. |
|||
Flexural Modulus | 5.80 GPa @Temperature 23.0 °C |
841 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF12030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL24 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL24 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Flexural Modulus | 5.80 GPa @Temperature 23.0 °C |
841 ksi @Temperature 73.4 °F |
ISO 178 |
DuPont Performance Polymers Sorona® 3015GV NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data**) Sorona® 3015GV NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength, stiffness and sur.. |
|||
Flexural Modulus | 5.80 GPa @Temperature 23.0 °C |
841 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF10030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
Inno-Comp INNOPOL® CS 1-5830 30% Glass-Fiber-Filled Polypropylene Homopolymer INNOPOL® CS 1-5830 is a 30% glass-fiber-filled polypropylene homopolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 1-5830 is recommended for producing in.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
Lanxess Durethan® BG 30 X H3.0 000000 Nylon 6, 30% Glass Fibers/Glass Spheres PA 6, 30% glass fibers/glass spheres, injection molding, heat-ageing stabilized, low tendency to warp |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
Solvay TECHNYL® B 218L V20 Black 44 N PA66, 25% glass fiber, DRY Description: Copolyamide 66/6, reinforced with 20% of glass fiber, for injection molding, heat stabilized with improved UV ageing resistanceAvailable in: Asia Pacific and EuropeProduct Applications:.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Asia Pacific) LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM CRS5201 PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. Resin is RoHS compliant. UL94 V0 and 5VA li.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM CRS5201R PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. Resin is RoHS com.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF004Z PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004Z is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: HV. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP PCAF04FRHH PC+ABS (Europe-Africa-Middle East) LNP* THERMOCOMP* PCA04FRHH is a 20 % glass reinforced PC+ABS blend without chlorinated or brominated flame retardants. LNP* THERMOCOMP* complies with the material requirements as specified in TCO'99.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP PF004 PA 6 (Europe-Africa-Middle East) 20% glass fibre reinforced Polyamide 6 injection moulding resin. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS (Europe-Africa-Middle East) LNP* THERMOCOMP* ZF004 is a compound based on PPE+PS Blend resin containing Glass Fiber. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Asia Pacific) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
Polyram RamSter RF303G6 PBT, 30% Glass Fiber, Industrial Grade Industrial Grade, 30% glass fiber reinforced PBT for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ASTM-D790 |
Polyram PlusTek PD300G6 Nylon 12, 30% Glass Fiber 30% glass-fiber reinforced polyamide 12 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 5.80 GPa @Temperature 120 °C |
841 ksi @Temperature 248 °F |
ISO 178 |
DSM Stanyl® TE200F8 PA46-GF40 40% Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | cond; ISO 178 |
DSM Stanyl® TS241B3 PA46-CF15 15% Carbon Reinforced, Lubricated |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® HTN 51G15HSL BK083 Polyphthalamide (PPA)
(Unverified Data**) 15% Glass Reinforced PPA High Performance Polyamide Zytel HTN51G15HSL BK083 is a 15% glass reinforced heat stabilized lubricated high performance polyamide resin. It is also a PPA resin.Information .. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO Data |
BASF Ultramid® 1403-2 BK ND3007 PA66 (Dry) |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO Data |
BASF Ultramid® 1403-2 NF3001 13% Glass Filled PA66 (Dry) Ultramid 1403-2 NF3001 is a 13% glass reinforced, heat stabilized injection molding PA6/6. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ASTM D790 |
Ashley Polymers Ashlene® P123 PBT Polyester, 15% Glass Reinforced PBT polyester with 15% glass reinforcement.Data provided by the manufacturer |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | |
Plastcom SLOVAMID 6 NG GF 20 PA6, 20% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data**)& 15% Glass Reinforced Polytrimethylene Terephthalate with Resin Made from Bio-PDO Sorona 3015G NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% ba.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data** 15% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Developed for Food Contact Applications Sorona FG3015G NC010 is a 15% glass fiber reinforced polytrimethylene terephthalate resi.. |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | cond; ISO 178 |
DSM Stanyl® TS200B3 PA46-CF15 15% Carbon Reinforced |
|||
Flexural Modulus | 5.80 GPa | 841 ksi | ASTM D790 |
Ashley Polymers Ashlene® P1420 Polycarbonate, 20% Glass Reinforced A 20% glass reinforced polycarbonate for increased mechanical strength and thermal properties. P1423: with UV stabilizer.Data provided by the manufacturer |