- Solvay TECHNYL® B 218L V20 Black 44 N PA66, 25% glass fiber, DRY
Solvay TECHNYL® B 218L V20 Black 44 N PA66, 25% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® B 218L V20 Black 44 N PA66, 25% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Copolyamide 66/6, reinforced with 20% of glass fiber, for injection molding, heat stabilized with improved UV ageing resistanceAvailable in: Asia Pacific and EuropeProduct Applications: TECHNYL B 218L V20 noir 44 N is used in all sectors of industry, offering an excellent combination of thermal and mechanical properties. This grade is commonly used for automotive applications which require a good surface appearance and a good UV resistance, such as: - external mirror housings and door handles. This product is available in black color.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183/A |
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 Type 1A |
| Flexural Modulus | 5.80 GPa | 841 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 242 °C | 468 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
1210 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 3.00e+13 ohm | 3.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 250 - 270 °C | 482 - 518 °F | |
| Front Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 260-270°C |
Users viewing this material also viewed the following:
- PolyOne Geon™ HTX M6307 Polyvinyl Chloride Alloy (PVC Alloy)
- LyondellBasell Pro-faxâ„¢ SR257M Polypropylene Copolymer
- Kingfa FRHIPS-100 Flame Retardant Polystyrene
- A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer
- A. Schulman SCHULAMID® 66 MK30HI 30% Mineral Reinforced, Impact Modified Nylon 66
- Polyplastics Duranex® 3405 Polybutylene Terephthalate (PBT), Standard, 45% GF filled
- CLAL-MSX NICLAFOR® 1000 THX Quenched/Precipitation Heat Treated, Drawn Copper Alloy
- Clariant Renol PA111G33 Nylon 66, 33% Glass Fiber
- BASF 1,5-Pentanediol (PDO)
- Lucite International Colacryl ® TS1171 Acrylic Solution Resin
Copyright © lookpolymers.com All Rights Reserved