SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
1.37 g/cc
0.0495 lb/in³
ASTM D792
Moisture Absorption 0.600 %
0.600 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
0.0064 cm/cm

@Time 86400 sec
0.0064 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.016 - 0.018 cm/cm

@Time 86400 sec
0.016 - 0.018 in/in

@Time 24.0 hour
ASTM D955
0.017 cm/cm

@Time 86400 sec
0.017 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 118 MPa
17100 psi
ISO 527
119 MPa
17300 psi
ASTM D638
Tensile Strength, Yield 118 MPa
17100 psi
ISO 527
119 MPa
17300 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ISO 527
3.1 %
3.1 %
ASTM D638
Elongation at Yield 3.0 %
3.0 %
ISO 527
3.1 %
3.1 %
ASTM D638
Tensile Modulus 6.44 GPa
934 ksi
1 mm/min; ISO 527
6.89 GPa
999 ksi
50 mm/min; ASTM D638
Flexural Strength 179 MPa
26000 psi
ASTM D790
183 MPa
26500 psi
ISO 178
Flexural Modulus 5.51 GPa
799 ksi
ASTM D790
5.80 GPa
841 ksi
ISO 178
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.71 J/cm
10.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J
5.16 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.39
0.39
ASTM D3702 Modified
Coefficient of Friction, Static 0.45
0.45
ASTM D3702 Modified
K (wear) Factor 38.3 x 10-8 mm³/N-M
19.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 39.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
21.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
39.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
22.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
261 °C

@Thickness 3.20 mm
502 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 243 °C
469 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
247 °C

@Thickness 3.20 mm
477 °F

@Thickness 0.126 in
unannealed; ASTM D648