DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)&

Category Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer DuPont Performance Polymers
Trade Name Sorona®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)  (Unverified Data**)&.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced Polytrimethylene Terephthalate with Resin Made from Bio-PDO Sorona 3015G NC010 is a 15% glass reinforced PTT resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) with good strength stiffness andInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption at Saturation 0.080 %
0.080 %
Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
ISO 527-1/-2
Tensile Stress 3.9278 MPa

@Strain 0.200 %,
Temperature 150 °C
 569.68 psi

@Strain 0.200 %,
Temperature 302 °F
 ISO 11403-1 -2
10.886 MPa

@Strain 0.600 %,
Temperature 150 °C
 1578.9 psi

@Strain 0.600 %,
Temperature 302 °F
 ISO 11403-1 -2
15.22 MPa

@Strain 0.900 %,
Temperature 150 °C
 2207 psi

@Strain 0.900 %,
Temperature 302 °F
 ISO 11403-1 -2
18.885 MPa

@Strain 1.20 %,
Temperature 150 °C
 2739.0 psi

@Strain 1.20 %,
Temperature 302 °F
 ISO 11403-1 -2
30.234 MPa

@Strain 0.500 %,
Temperature 23.0 °C
 4385.1 psi

@Strain 0.500 %,
Temperature 73.4 °F
 ISO 11403-1 -2
30.725 MPa

@Strain 0.500 %,
Temperature 0.000 °C
 4456.3 psi

@Strain 0.500 %,
Temperature 32.0 °F
 ISO 11403-1 -2
41.156 MPa

@Strain 0.700 %,
Temperature 40.0 °C
 5969.2 psi

@Strain 0.700 %,
Temperature 104 °F
 ISO 11403-1 -2
44.857 MPa

@Strain 0.700 %,
Temperature -40.0 °C
 6506.0 psi

@Strain 0.700 %,
Temperature -40.0 °F
 ISO 11403-1 -2
56.918 MPa

@Strain 1.00 %,
Temperature 40.0 °C
 8255.3 psi

@Strain 1.00 %,
Temperature 104 °F
 ISO 11403-1 -2
57.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 8270 psi

@Strain 1.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
63.134 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 9156.8 psi

@Strain 1.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
64.435 MPa

@Strain 1.10 %,
Temperature 0.000 °C
 9345.5 psi

@Strain 1.10 %,
Temperature 32.0 °F
 ISO 11403-1 -2
70.223 MPa

@Strain 1.30 %,
Temperature 40.0 °C
 10185 psi

@Strain 1.30 %,
Temperature 104 °F
 ISO 11403-1 -2
71.233 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 10331 psi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
79.772 MPa

@Strain 1.40 %,
Temperature 0.000 °C
 11570 psi

@Strain 1.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
80.407 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 11662 psi

@Strain 1.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
81.404 MPa

@Strain 1.60 %,
Temperature 40.0 °C
 11807 psi

@Strain 1.60 %,
Temperature 104 °F
 ISO 11403-1 -2
84.755 MPa

@Strain 1.60 %,
Temperature 23.0 °C
 12293 psi

@Strain 1.60 %,
Temperature 73.4 °F
 ISO 11403-1 -2
93.907 MPa

@Strain 1.70 %,
Temperature 0.000 °C
 13620 psi

@Strain 1.70 %,
Temperature 32.0 °F
 ISO 11403-1 -2
96.686 MPa

@Strain 1.60 %,
Temperature -40.0 °C
 14023 psi

@Strain 1.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 6.50 GPa
943 ksi
ISO 527-1/-2
Flexural Strength 190 MPa
27600 psi
ISO 178
Flexural Modulus 5.80 GPa
841 ksi
ISO 178
Secant Modulus 1.4435 GPa

@Strain 3.20 %,
Temperature 100 °C
 209.37 ksi

@Strain 3.20 %,
Temperature 212 °F
 ISO 11403-1 -2
1.56 GPa

@Strain 3.50 %,
Temperature 80.0 °C
 227 ksi

@Strain 3.50 %,
Temperature 176 °F
 ISO 11403-1 -2
1.67 GPa

@Strain 2.40 %,
Temperature 100 °C
 243 ksi

@Strain 2.40 %,
Temperature 212 °F
 ISO 11403-1 -2
1.80 GPa

@Strain 2.70 %,
Temperature 80.0 °C
 262 ksi

@Strain 2.70 %,
Temperature 176 °F
 ISO 11403-1 -2
1.95 GPa

@Strain 1.60 %,
Temperature 100 °C
 283 ksi

@Strain 1.60 %,
Temperature 212 °F
 ISO 11403-1 -2
2.07 GPa

@Strain 1.90 %,
Temperature 80.0 °C
 300 ksi

@Strain 1.90 %,
Temperature 176 °F
 ISO 11403-1 -2
2.29 GPa

@Strain 0.800 %,
Temperature 100 °C
 332 ksi

@Strain 0.800 %,
Temperature 212 °F
 ISO 11403-1 -2
2.41 GPa

@Strain 1.10 %,
Temperature 80.0 °C
 350 ksi

@Strain 1.10 %,
Temperature 176 °F
 ISO 11403-1 -2
2.4809 GPa

@Strain 0.100 %,
Temperature 100 °C
 359.83 ksi

@Strain 0.100 %,
Temperature 212 °F
 ISO 11403-1 -2
2.6388 GPa

@Strain 0.500 %,
Temperature 80.0 °C
 382.73 ksi

@Strain 0.500 %,
Temperature 176 °F
 ISO 11403-1 -2
4.16 GPa

@Strain 2.40 %,
Temperature 40.0 °C
 604 ksi

@Strain 2.40 %,
Temperature 104 °F
 ISO 11403-1 -2
4.67 GPa

@Strain 2.40 %,
Temperature 23.0 °C
 677 ksi

@Strain 2.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
4.98 GPa

@Strain 1.70 %,
Temperature 40.0 °C
 722 ksi

@Strain 1.70 %,
Temperature 104 °F
 ISO 11403-1 -2
5.05 GPa

@Strain 2.40 %,
Temperature 0.000 °C
 733 ksi

@Strain 2.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
5.23 GPa

@Strain 1.70 %,
Temperature 23.0 °C
 758 ksi

@Strain 1.70 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.40 GPa

@Strain 1.30 %,
Temperature 40.0 °C
 783 ksi

@Strain 1.30 %,
Temperature 104 °F
 ISO 11403-1 -2
5.46 GPa

@Strain 1.80 %,
Temperature 0.000 °C
 792 ksi

@Strain 1.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
5.48 GPa

@Strain 1.30 %,
Temperature 23.0 °C
 795 ksi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.698 GPa

@Strain 1.40 %,
Temperature 0.000 °C
 826.4 ksi

@Strain 1.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
5.78 GPa

@Strain 0.900 %,
Temperature 40.0 °C
 839 ksi

@Strain 0.900 %,
Temperature 104 °F
 ISO 11403-1 -2
5.80 GPa

@Strain 2.10 %,
Temperature -40.0 °C
 842 ksi

@Strain 2.10 %,
Temperature -40.0 °F
 ISO 11403-1 -2
5.813 GPa

@Strain 0.900 %,
Temperature 23.0 °C
 843.1 ksi

@Strain 0.900 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.9006 GPa

@Strain 1.00 %,
Temperature 0.000 °C
 855.82 ksi

@Strain 1.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
6.00 GPa

@Strain 1.70 %,
Temperature -40.0 °C
 870 ksi

@Strain 1.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
6.05 GPa

@Strain 0.600 %,
Temperature 40.0 °C
 877 ksi

@Strain 0.600 %,
Temperature 104 °F
 ISO 11403-1 -2
6.19 GPa

@Strain 1.30 %,
Temperature -40.0 °C
 897 ksi

@Strain 1.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
6.20 GPa

@Strain 0.100 %,
Temperature 23.0 °C
 899 ksi

@Strain 0.100 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.3026 GPa

@Strain 0.100 %,
Temperature 0.000 °C
 914.13 ksi

@Strain 0.100 %,
Temperature 32.0 °F
 ISO 11403-1 -2
6.34 GPa

@Strain 0.900 %,
Temperature -40.0 °C
 920 ksi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
6.881 GPa

@Strain 0.200 %,
Temperature -40.0 °C
 998.0 ksi

@Strain 0.200 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
ISO 179/1eU
3.00 J/cm²

@Temperature -30.0 °C
 14.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA