Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.20 GPa @Temperature 23.0 °C |
464 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH TS15040 D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
Flexural Modulus | 3.20 GPa @Temperature 23.0 °C |
464 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH TS15040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
Nilit FRIANYL B63 KG30 Nylon 6 for injection molding, 30% chalk filled Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
SABIC Innovative Plastics LNP COLORCOMP R1000S PA 66 LNP COLORCOMP* R1000S is an unfilled Nylon 66. Added features of this material is: Heat Stabilized. |
|||
Flexural Modulus | 3.20 - 8.30 GPa | 464 - 1200 ksi | Average value: 5.57 GPa Grade Count:3 |
Overview of materials for Polystyrene, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Wood Filled". Each property range of values reported is minimum and maximum values of appro.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178, ASTM D790 |
Nilit Nilamid A3 N H2 Nucleated, Heat Stabilized Nylon 66 Description: Nilamid A3 N H2 is a nucleated, heat stabilized NYLON 66 with excellent flow characteristics and very fast cycle time. It is widely used throughout many industries for mass production a.. |
|||
Flexural Modulus | 3.20 GPa @Temperature 23.0 °C |
464 ksi @Temperature 73.4 °F |
ISO 178 |
DuPont Performance Polymers Delrin® 511DP BK402 Acetal Homopolymer
(Unverified Data**) Delrin® 511DP is a medium viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, less shrinkage, fewer voids).Information provided.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | DIN 53 457 |
Albis Plastics Tedur® L V 9900-1 PPS, Unreinforced
(discontinued **) Excellent Surface Finish, High Chemical Resistance. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Pipes, ProfilesProcessing: Extrusion (Melt Temperature: 555-610°F).. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
I. Stern N1921 General Purpose Crystal Polystyrene Features:Excellent ProcessabilityEasy FlowApplicationsDisposable PackagingHousewaresCosmetics PackagingAgency RatingsFDA Title 21 CFR 177.1640UL File E220962Information provided by I. Stern & Co. In.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | 2mm/min; ASTM D790 |
Kingfa PA66-ROW Halogen-free, Flame Retardant PA66 Features:Flame retardantHigh mechanical strengthHigh heat resistanceGood electric propertiesNo bloomingApplications:Injection moldingConnectors, linkersRelay, bobbins, plugsHousehold appliance parts.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
Lucite International Diakon® MG100 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
Lucky EF-940 Acrylic, Injection/Extrusion Grade Extrusion and injection grade. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capa.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East) High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM LTX300B PEI Standard flow Polyetherimide blend with low toxicity, smoke, and flame evolution. ECO Compliant, UL94 V0 listing. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene DescriptionPolyfort® FPP 1068-32 Black is a 40% mineral filled polypropylene designed for use when improved heat resistance, dimensional stability and high stiffness is needed. ApplicationApplicati.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178-93 |
Wellman Wellamid® FR1841-N1 Nylon 66, Unfilled, Flame Retardant All information provided by Wellman Engineered Resins. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178-93 |
Wellman Wellamid® FR22F-NBK3 Flame Retardant Nylon 66 Description: Flame Retardant Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178-93 |
Wellman Wellamid® GF10-42LI4-N-Gray 10% Glass Reinforced, Toughened Nylon 6 Description: Glass Reinforced, Toughened Nylon 6Information provided by Wellman. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1068-32 Black40% Mineral Filled Polypropylene DescriptionPolyfort® FPP 1068-32 Black is a 40% mineral filled polypropylene designed for use when improved heat resistance, dimensional stability and high stiffness is needed. ApplicationApplicati.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
DSM Stanyl® TE263F6 (COND) Nylon 46 30% Glass Reinforced, Heat Stabilized, Impact Modified (North America) Information provided by DSM Engineering Plastics. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600 GS 20 HWCP 20% Glass Sphere Filled Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 |
Eurostar Staramide AS3 PA66, 15% Glass Bead Reinforced, Injection Molding Staramide AS3 is a 15% Glass Bead Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
Cast Nylons Nycast® 6PA-MoS2 Nylon 6 NYCAST® 6PA-MoS2 is a molybdenum disulphide filled Type 6 cast nylon. Finely divided MoS2 particles are suspended in the melt during polymerization. This gives the NYCAST® 6PA-MoS2 products improv.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, DAM Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 43% Filler by Weight Additive:Nucleating AgentLubricant Features:Fast Molding CycleGeneral PurposeGood Mold Release Good.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
Ascend Performance Materials Vydyne® ECO315 BK06 Nylon 66/6, Flame Retardant, DAM Vydyne® ECO315 BK06 is a non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent toughness and ductility. It is lubricated for machine feed and easy mold release and has Underwri.. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
Ashley Polymers Ashlene® D870, D870L, Transparent Amorphous Nylon D870 = Transparent Amorphous Nylon for Injection Molding, Unlubricated. D870L = Transparent Amorphous Nylon for Injection Molding, Lubricated.Data provided by the manufacturer |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP JF002R PES (Europe-Africa-Middle East) LNP* Thermocomp* JF002R is a compound based on Polyethersulfone resin containing Glass Fiber, Glass Bead. Added features of this material include: Mold Release. |
|||
Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
Buckeye Polymers BP RPP 4012 TU Polypropylene, 40% Mineral Filled UV StabilizedThis Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistan.. |