SABIC Innovative Plastics LNP THERMOCOMP JF002R PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP JF002R PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* JF002R is a compound based on Polyethersulfone resin containing Glass Fiber, Glass Bead. Added features of this material include: Mold Release.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength, Yield 83.0 MPa
12000 psi
5 mm/min; ISO 527
Elongation at Yield 4.5 %
4.5 %
5 mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
Flexural Strength 74.0 MPa
10700 psi
2 mm/min; ISO 178
Flexural Yield Strength 133 MPa
19300 psi
2 mm/min; ISO 178
Flexural Modulus 3.20 GPa
464 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 23.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 30.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 212 °C
414 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af