Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
3M Dyneon™ Fluorel™ FE-5840Q Fluoroelastomer VF2 + HFP + TFE Terpolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 70.1%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
3M Dyneon™ Fluorel™ FC-2152 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Improved hot tear over FC-2176. Sugg.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
3M Dyneon™ Fluorel™ FC-2230 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escor® AT-310 EMAAA Terpolymer for Polymer Modification
(discontinued **) Data provided by the manufacturer, Exxon Chemical.45 Acid Number. Provides unusual adhesion to a variety of substrates and other components such as aluminum foil, polyolefins, polycarbonate, PET, e.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE 1008 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Superior strength, good machinability, and heat seal characteristics.Applications: Film extrusion: industrial packaging, frozen food, produce bags, shrink, a.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escorene® LD-725 High EVA Film and Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An 18% vinyl acetate copolymer designed for specialty film and compounding applications. Outstanding sealability and low modulus are key attributes.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escorene® LD-767 High EVA Film and Compounding Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A low gel 29.5% vinyl acetate copolymer designed for film and compounding applications. The resin provides very low modulus films with high tensile.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE1205 EVA Film Extrusion
(discontinued **) 2% Vinyl Acetate EVA copolymer and FDA compliantFeatures: High clarity film with good stiffness and low temperature toughness.Applications: Film extrusion: food packaging, general purpose packaging .. |
|||
Tensile Strength, Ultimate | 14.0 - 26.0 MPa | 2030 - 3770 psi | Average value: 18.9 MPa Grade Count:11 |
Overview of materials for Polypropylene, Mineral Reinforced, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced, Impact Modified". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 14.0 - 30.0 MPa | 2030 - 4350 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 31008 PVDF Copolymer
(discontinued **) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General .. |
|||
Tensile Strength, Ultimate | 14.0 - 30.0 MPa | 2030 - 4350 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 32008 PVDF Copolymer
(Unverified Data**) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General .. |
|||
Tensile Strength, Ultimate | 14.0 - 250 MPa @Temperature -40.0 - 250 °C |
2030 - 36300 psi @Temperature -40.0 - 482 °F |
Average value: 83.4 MPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an.. |
|||
Tensile Strength, Ultimate | 14.0 - 250 MPa @Thickness 0.800 - 3.17 mm |
2030 - 36300 psi @Thickness 0.0315 - 0.125 in |
Average value: 83.4 MPa Grade Count:3 |
Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
LyondellBasell Astryn SZ021-2 Polypropylene Copolymer, 20% Talc Key Features: medium melt flow, medium modulus, mineral-filled, utility grade polypropylene copolymer, good impact and stiffness balance, versatileApplications: inner door panels and seat supportsDe.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | DIN 53504 |
Lubrizol ESTANE® T4086 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | butt tensile strength per ASTM D426 on brass |
Von Roll Isola IMI E-Solder® 3021 Electrically Conductive Adhesive Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t.. |
|||
Tensile Strength, Ultimate | >= 14.0 MPa | >= 2030 psi | |
Von Roll Isola IMI Irrathene® 210 Irradiated Polyethylene Film, Encapsulation Grade Data provided by Von Roll Isola USA.Produced by electron bombardment of specially formulated polyethylene film used in a wide variety of electrical applications. Irrathene film is nonmelting and hi.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | Type IV, crosshead speed 2 in/min; ASTM D638 |
DuPont Elvax® 550 Ethylene-Vinyl Acetate Copolymer Resin Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | GB/T 528 |
Chengdu Polyster 8500 General Grade TPV Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638/D412 |
Covestro Baydur® 730 IBS Polyurethane Structural Foam RIM, Density 35 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience .. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 109 Polypropylene, Mineral Reinforced, Impact Modified Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | |
BASF Lucalen® A 2710 H Ethylene/Acrylate Copolymer Product with properties which are typical of flexible PVC and of low density polyethylene. Suitable for flexible pipes, profiles and seals.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
Huntsman PE7011 Profile Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Excellent strength, good machinability, and foaming characteristics.Applications: Extrusion: profile extrusion.FDA Notes: Conforms to FDA regulation 21 CFR 17.. |
|||
Tensile Strength, Ultimate | 14.0 - 280 MPa | 2030 - 40600 psi | Average value: 237 MPa Grade Count:18 |
Overview of materials for Polyvinyl Dichloride (PVDC) This property data is a summary of similar materials in the MatWeb database for the category "Polyvinyl Dichloride (PVDC)". Each property range of values reported is minimum and maximum values of ap.. |
|||
Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
ExxonMobil Escorene® UL-7560 EVA Copolymer, Adhesive and Sealant Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.An 18% vinyl acetate copolymerApplications: Hot melt adhesives; Wax blends; Industrial sealants. |
|||
Tensile Strength, Ultimate | 14.0 - 33.8 MPa | 2030 - 4900 psi | Average value: 26.2 MPa Grade Count:22 |
Overview of materials for Polypropylene with 30% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Mica Filler". Specific grades with primary filler content between 25% and 34% are.. |
|||
Tensile Strength, Ultimate | 14.0 - 32.4 MPa | 2030 - 4700 psi | Average value: 26.4 MPa Grade Count:21 |
Overview of materials for Polypropylene with 40% Mica Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Mica Filler". Specific grades with primary filler content between 35% and 44% are.. |