DSM Arnitel® PL381-H TPC-ET
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnitel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnitel® PL381-H TPC-ET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Sim. To ISO 62 |
| Moisture Absorption | 0.400 % | 0.400 % | Sm. To ISO 62 |
| Melt Flow | 32 g/10 min @Load 2.16 kg, Temperature 230 °C |
32 g/10 min @Load 4.76 lb, Temperature 446 °F |
cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 32 @Time 3.00 sec |
32 @Time 0.000833 hour |
ISO 868 |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ISO 527-1/-2 |
| Tensile Stress | 4.20 MPa @Strain 10.0 % |
609 psi @Strain 10.0 % |
ISO 527-1/-2 |
| 8.40 MPa @Strain 100 % |
1220 psi @Strain 100 % |
ISO 527-1/-2 | |
| Elongation at Break | 450 % | 450 % | ISO 527-1/-2 |
| Tensile Modulus | 0.0600 GPa | 8.70 ksi | ISO 527-1/-2 |
| Izod Impact Resistance | NB | NB | ISO 180/1A |
| NB | NB | ISO 180/1A | |
| Charpy Impact, Notched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eA |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 212 °C | 414 °F | 10°C/min; ISO 11357-1/-3 |
| Vicat Softening Point | 124 °C | 255 °F | 50 °C/h 10N; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Dielectric Constant | 4.4 @Frequency 1.00e+6 Hz |
4.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.7 @Frequency 100 Hz |
4.7 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.031 @Frequency 100 Hz |
0.031 @Frequency 100 Hz |
IEC 60250 |
| 0.081 @Frequency 1.00e+6 Hz |
0.081 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8521BL (UF) Synthetic Oil
- Omnia Plastica PC Polycarbonate
- Precision Polymer Engineering E70A Ethylene Propylene Rubber
- Lehmann & Voss LUVOCOM® 20-7638 Polyphthalamide, with carbon fiber and PTFE
- Haynes 214® alloy, 50% cold reduction
- Teknor Apex Monprene® MP-2238-R Thermoplastic Elastomer
- Borealis Borclean™ HB300BF Polypropylene Homopolymer for Capacitor Film
- DSM Akulon® K223-HM6 (BLACK) Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Cond)
- Daikin NEOFLON NP-101 FEP Pellets
- Abatron AboCast 50-6/AboCure 50-12 Epoxy
Copyright © lookpolymers.com All Rights Reserved