Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC, Powder". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.42 - 1.81 g/cc
0.0513 - 0.0654 lb/in³
Average value: 1.50 g/cc Grade Count:13
Volatile Organic Compounds (VOC) Content 0.0300 - 0.300 g/l
0.0300 - 0.300 g/l
Average value: 0.290 g/l Grade Count:26
Apparent Bulk Density 0.550 - 0.780 g/cc
0.0199 - 0.0282 lb/in³
Average value: 0.650 g/cc Grade Count:5
Particle Size 0.100 - 250 µm
0.100 - 250 µm
Average value: 111 µm Grade Count:27
Viscosity Test 109 - 136 cm³/g
109 - 136 cm³/g
Average value: 124 cm³/g Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Shore D 73.0 - 84.0
73.0 - 84.0
Average value: 79.7 Grade Count:15
Tensile Strength, Ultimate 14.0 - 51.0 MPa
2030 - 7400 psi
Average value: 38.4 MPa Grade Count:15
Modulus of Elasticity 1.12 - 3.66 GPa
163 - 531 ksi
Average value: 2.69 GPa Grade Count:10
Flexural Yield Strength 28.0 - 98.0 MPa
4060 - 14200 psi
Average value: 74.5 MPa Grade Count:10
Flexural Modulus 1.21 - 3.78 GPa
175 - 548 ksi
Average value: 2.76 GPa Grade Count:9
Izod Impact, Notched 0.200 - 4.90 J/cm
0.375 - 9.18 ft-lb/in
Average value: 1.64 J/cm Grade Count:9
Thermal Properties Metric English Comments
CTE, linear 54.0 - 62.0 µm/m-°C
30.0 - 34.4 µin/in-°F
Average value: 57.2 µm/m-°C Grade Count:8
Deflection Temperature at 1.8 MPa (264 psi) 51.0 - 74.0 °C
124 - 165 °F
Average value: 70.3 °C Grade Count:10
Processing Properties Metric English Comments
Melt Temperature 182 - 210 °C
360 - 410 °F
Average value: 195 °C Grade Count:9