Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1924P Polyethylene
(discontinued **) Low-density polyethylene 1924P is a resin in the boardstock coating industry for use in breadboard, cupstock, and liquid packaging board. This material has an excellent combination of low neck-in, .. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 808A Polyethylene
(discontinued **) Low density polyethylene 808A is a general-purpose formulation used for injection molding and general-purpose extrusion.Unless otherwise noted, all tests are run at 23°C and 50% RH.Information from.. |
|||
Tensile Strength, Ultimate | 10.0 - 182 MPa | 1450 - 26400 psi | Average value: 103 MPa Grade Count:57 |
Overview of materials for Acetal Copolymer, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% ar.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Global MM-1018 Low Density Polyethylene, Lamination Coating Grade
(discontinued **) Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-laminates, coating applications, food applicationsMeets FDA requirements as listed i.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Global JJ-4324 Low Density Polyethylene, Film Extrusion Grade
(discontinued **) Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-bagsMeets FDA requirements as listed in food additives regulation 21 CFR 117.1520 fo.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE1044 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Yields film with excellent optical and machinability.Applications: Film extrusion: soft goods and other high clarity packaging.FDA Notes: Conforms to FDA reg.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE1065 Film Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with excellent optical and machinability.Applications: Film extrusion: soft goods and other high clarity packaging.FDA Notes: Conforms to FDA regu.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE5080 Extrusion Coating Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Excellent draw down, low neck-in, and excellent adhesion.Applications: Extrusion: coating grade and thin coatings.FDA Notes: Conforms to FDA regulation 21 CFR.. |
|||
Tensile Strength, Ultimate | 10.0 - 105 MPa @Temperature 60.0 - 150 °C |
1450 - 15200 psi @Temperature 140 - 302 °F |
Average value: 50.2 MPa Grade Count:6 |
Overview of materials for Nylon 6, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 10.0 - 95.0 MPa @Temperature -20.0 - 100 °C |
1450 - 13800 psi @Temperature -4.00 - 212 °F |
Average value: 49.1 MPa Grade Count:1 |
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
Tensile Strength, Ultimate | 10.0 - 95.0 MPa @Strain 1.00 - 3.00 % |
1450 - 13800 psi @Strain 1.00 - 3.00 % |
Average value: 49.1 MPa Grade Count:1 |
Overview of materials for Nylon 66, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum .. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 5703 BLK The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ISO 527-1 |
Chengdu Polyster CH4132 Thermoplastic Polyether-ester Elastomer (TPEE) Poly-basic block copolymer. Good compatibility with POM. For blending with POM to improve impact resilience properties.Information provided by Chengdu Polyster Co., Ltd. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | |
Dow Corning SILASTIC® LSR 9791-70 A&B KIT 70 Durometer, 2-part, 1 to 1 mix, translucent, molding grade, Liquid Silicone Rubber.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | |
Dow DOWLEX™ IP-42 High Density Polyethylene DOWLEX® IP-42 resin is an improved processing high density polyethylene resin designed for excellent flow and high impact. DOWLEX IP-42 resin is designed by optimizing the breadth and shape of the .. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | |
Dow DOWLEX™ IP-60 High Density Polyethylene DOWLEX® IP-60 resin is an improved processing high density polyethylene resin designed to offer excellent processability, good impact and top load strength required in thin wall injection molding. .. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | |
Dow DOWLEX™ IP-90 High Density Polyethylene Next Generation DOWLEX® IP-90 resin is a high flow improved processing high density polyethylene resin designed for ultra-thin wall injection molded containers and drink cups. This resin has been m.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE2040 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Good molding processability, produces parts that are flexible, and show excellent flatness in large projected areas.Applications: Injection molding: general p.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE2065 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: General purpose injection molding resin with good flow characteristicsApplications: Injection molding: lids.FDA Notes: Conforms to FDA regulation 21 CFR 177.1.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D 5308 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 10.0 - 43.0 MPa | 1450 - 6240 psi | Average value: 21.4 MPa Grade Count:141 |
Overview of materials for High Density Polyethylene (HDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Injection Molded". Each property range of values reported is minimum a.. |
|||
Tensile Strength, Ultimate | 10.0 - 30.0 MPa | 1450 - 4350 psi | Average value: 22.5 MPa Grade Count:11 |
Overview of materials for Polymethylpentene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polymethylpentene, Molded". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Ultimate | 10.0 - 135 MPa @Temperature 60.0 - 150 °C |
1450 - 19600 psi @Temperature 140 - 302 °F |
Average value: 70.2 MPa Grade Count:2 |
Overview of materials for Polyethersulfone (PES), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% .. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE2038 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: High mechanical flexing properties, excellent processability, good stress crack resistance, and very good low temperature strength.Applications: Injection mol.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE2053 Injection Molding Polyethylene
(discontinued **) Homopolymer, Drug Master File listed product, and FDA compliant.Features: High flow characteristics, good gloss, and processability.Applications: Injection molding: large moldings including housewar.. |
|||
Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | ASTM D638 |
Huntsman PE2062 Injection Molding Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: High flow characteristics combined with good glossApplications: Injection molding: large moldings including housewares and toys.FDA Notes: Conforms to FDA reg.. |
|||
Tensile Strength, Ultimate | 10.0 - 100 MPa @Strain 1.00 - 8.00 % |
1450 - 14500 psi @Strain 1.00 - 8.00 % |
Average value: 45.0 MPa Grade Count:2 |
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 10.0 - 65.0 MPa | 1450 - 9430 psi | Average value: 23.8 MPa Grade Count:133 |
Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |