Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
Nylene® Vexel™ B12GF15 FR , 15% Glass Reinforced, Flame Retardant PBT Description: Vexel™ B12GF15 FR is a 15% glass fiber reinforced flame retardant PBT. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polyme.. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® PS-15GF-25MN/000 Polybutylene Terephthalate (PBT), Glass/Mineral Filled
(discontinued **)< Description/Features:Glass/Mineral ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® AS-13CF/000 Acrylonitrile Butadiene Styrene (ABS), Carbon Fiber Reinforced
(discontinued **) Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Stat-Tech™ CTX 1125 PC/ABS Blend, Carbon Fiber Reinforced
(discontinued **) Description/Features:Electrically ConductiveNickel Coated Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 89.6 - 193 MPa | 13000 - 28000 psi | Average value: 121 MPa Grade Count:58 |
Overview of materials for Polycarbonate, Carbon + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon + PTFE Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | |
CE Phenolic Laminate Cotton based phenolic provides more mechanical strength than paper grades and has a finer surface with better machinability. This material is used for gears, pinions, bearings, bushings, and many s.. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
Adell AJ-13 Nylon 66, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
Adell AJ-33 Nylon 66, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
Adell ER-36 Homopolymer Polypropylene, 30% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
Applied Composites 179 Polyester SMC Industry Application: TransportationProduct Application: Auto InteriorsInformation provided by Applied Composites Corporation. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
Applied Composites 8007 Polyester SMC Industry Application: ConstructionProduct Application: Water TreatmentDistinct Features: Pigmentable, Low Water Absorption, Weathering Resistant, Good Corrosion Resistance in Waste Water Environment.. |
|||
Tensile Strength, Ultimate | 89.6 MPa @Temperature 760 °C |
13000 psi @Temperature 1400 °F |
|
ATI Allegheny Ludlum AL 468™ Dual Stabilized- Low Titanium Stainless Steel Characteristics:good corrosion resistance in a wide range of environments, can be used in annealed cold formed or as-welded conditions. Applications: used in place of Type 304 in an oxidizing when .. |
|||
Tensile Strength, Ultimate | 89.6 - 125 MPa | 13000 - 18100 psi | Average value: 100 MPa Grade Count:8 |
Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are .. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Lubri-Tech™ RA-15GF/13T Polyethersulfone, Glass Filled, PTFE Lubricated
(discontinued **) Description/Features:Glass Fiber ReinforcedPTFE LubricatedUL 94 V0UL 94 (CTI Testing)PolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
Adell ER-17 Homopolymer Polypropylene, 30% Glass Reinforced Data provided by Adell Plastics, Inc. |