Adell AJ-13 Nylon 66, 15% Glass Reinforced; High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Reinforced, Impact Grade |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell AJ-13 Nylon 66, 15% Glass Reinforced; High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 81 | 81 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 121 MPa | 17500 psi | ASTM D790 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D790 |
| Compressive Yield Strength | 110 MPa | 16000 psi | ASTM D695 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 227 °C | 441 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 421 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Polymax® Maxelast® F02-081A-15B TPE, Halogen Free Extrusion Grade
- NanoAmor 95%, OD: 8-15 nm OH Functionalized Aligned Multi-Walled Carbon Nanotubes
- Honeywell Capran® Emblem™ 1200M Bi-Axially Oriented Nylon 6 Film
- Kuraray SEPTON® S2005 Thermoplastic Rubber
- A. Schulman POLYBATCH™ Blue 40343/4 Concentrate Based In Polyethylene
- ExxonMobil Pax-Plus™ 3204 Blown Film Resin
- DuPont Teijin Films Melinex® 534 Polyester Film, 380 Gauge
- Clariant Renol PBT1100S Polybutylene Terephthalate, Silicone Lubricated
- Arlon LW201B##-P0 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported)