- PolyOne Stat-Tech™ CTX 1125 PC/ABS Blend, Carbon Fiber Reinforced (discontinued **)
PolyOne Stat-Tech™ CTX 1125 PC/ABS Blend, Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ CTX 1125 PC/ABS Blend, Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Electrically ConductiveNickel Coated Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1500 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 5.0 ohm-cm | 1.0 - 5.0 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.0 - 5.0 ohm | 1.0 - 5.0 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Shielding Effectiveness | 40 - 70 db | 1,000 MHz |
Users viewing this material also viewed the following:
- MarkeTech Gallium Arsenide Semiconductor Wafer, n-type, Tellurium Doped, LEC Grown
- Karina E 837-10/168-A-ERYB-AS White PVC Compound
- MRC Polymers NAXALOYâ„¢ 793MF6 PC + Polyester Blend, 6% Mineral Filled
- Wieland 1932 Wilaform Palladium
- Hexcel® HexPly® 954-2A Curing Cyanate Resin
- ExxonMobil AP3AW Polypropylene Impact Copolymer
- Fainplast Compounds KL 0993 Flexible PVC, Insulation for High Temperatures Lead Free
- BNZ Materials BNZP-23L Insulating Firebrick (French Grade)
- BorsodChem ONGROSTYR F-I Expandable Polystyrene (EPS)
- Adamas Adalon® 805 PTFE, 40% Bronze
Copyright © lookpolymers.com All Rights Reserved