Adell ER-17 Homopolymer Polypropylene, 30% Glass Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell ER-17 Homopolymer Polypropylene, 30% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.13 g/cc | 0.0401 - 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 60 | 60 | ASTM D785 |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 89.6 MPa | 13000 psi | ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | 1/8 inch; ASTM D256 |
| Izod Impact, Unnotched | 4.27 J/cm | 8.00 ft-lb/in | 1/8 inch; ASTM D256 |
| Gardner Impact | 0.300 J | 0.221 ft-lb | ASTM D695 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 171 - 193 °C | 340 - 380 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 310 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ MD 4245-59770 Polypropylene Copolymer (PP Copolymer)
- NOVA Chemicals Sclair® FG220-A Octene LLDPE Film Resin
- Permabond 731 Cyanoacrylate, toughened
- LG Chemical LS170 PVC
- H.C. Starck Amperit® 105.2 Agglomerated Sintered Molybdenum (Mo)
- California Fine Wire Nickel Alloy 30 Copper Nickel Resistance Wire
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Non-Black, Precipitated Calcium Carbonate
- ExxonMobil ESCOR™ AT 310 Molding, extrusion and compounding resin (discontinued **)
- Resinlab® EP1115 Clear Unfilled Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved