Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polyester (Spray-up/Lay-up), 30 wt.% glass Data provided by the manufacturer, Owens Corning. |
|||
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
PolyOne Edgetek® AS-20GF/000 HI UV NAT Acrylonitrile Butadiene Styrene (ABS), Glass Filled
(discontinued **)& Description/Features:Glass Fiber ReinforcedHigh ImpactUV StabilizedNaturalUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Tensile Strength, Ultimate | 86.0 - 130 MPa | 12500 - 18900 psi | Average value: 111 MPa Grade Count:16 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%.. |
|||
Tensile Strength, Ultimate | 86.2 - 115 MPa | 12500 - 16700 psi | Average value: 101 MPa Grade Count:4 |
Overview of materials for Nylon 11 with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are includ.. |
|||
Tensile Strength, Ultimate | 86.0 MPa @Temperature 22.0 °C |
12500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP SMC 0390 is a standard low profile SMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surfac.. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
Glastic Laminates/Shapes SG-200 High Strength/High Temperature Polyester Laminate Data provided by Glastic Corporation.NEMA GPO-1. A superior replacement for epoxy-bonded mica in layer insulation applications. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
Saint-Gobain Meldin® 7001 Isostatically Molded Polyimide Finished parts and basic shapes made from unfilled polyimide material for structural applications requiring requiring high electrical insulative properties, high purity and low outgassing, and high .. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ISO 527-1, 2 |
Polyplastics Duranex® 7195W Polybutylene Terephthalate (PBT), Super low warpage, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
Adell BH-18 Nylon 6, 40% Mineral Filled Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
Adell BH-38 Nylon 6, 40% Mineral Filled Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
Adell BJ-33 Nylon 6, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | 5mm/min; ISO 527 |
BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Conditioned) Ultramid 7423-2 NF3001 is an impact modified, 13% glass reinforced, heat stabilized injection molding PA6/6. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ATSM D638 |
Ashley Polymers Ashlene® P123 PBT Polyester, 15% Glass Reinforced PBT polyester with 15% glass reinforcement.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ATSM D638 |
Ashley Polymers Ashlene® P284 PPE Alloy, 10% Glass Reinforced A 10% glass reinforced PPE Alloy for superior properties and chemical resistance with high heat resistance.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
Chem Polymer Chemlon 109-18 G Nylon 66, 18% Glass Fiber Reinforced A highly toughened 18% glass fiber reinforced nylon 66 developed for applications requiring stiffness, creep resistance and impact resistance.Data provided by the manufacturer, Chem Polymer. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
Chem Polymer Durlex 715 G PBT, 15% Glass Reinforced A lubricated, 15% glass reinforced PBT offering a balance of rigidity, dimensional stability and toughness.Data provided by the manufacturer, Chem Polymer. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
A. Schulman ComAlloy Comtuf® 635 Nylon 6/6, Glass/Mineral Reinforced, Impact Modified, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has .. |
|||
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
Adell BJ-13 Nylon 6, 15% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
Chem Polymer Chemlon 223 Nylon 6, Nucleated A highly nucleated, lubricated nylon 6 intended for applications requiring a faster cycle time. It has increased tensile strength, rigidity, creep resistance and hardness over general purpose nylon.. |
|||
Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ISO value at 5mm/min. |
BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron 8333G is a 33% glass reinforced nylon 6 modified compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness, and excel.. |
|||
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
Solvay Specialty Polymers Xydar® M-345 Liquid Crystal Polymer, 45% Mineral Filled
(discontinued **) XYDAR M-345 Liquid Crystal Polymer (LCP) is a 45% mineral-filled injection molding grade with exceptional moldability. XYDAR M-345 resin can fill very thin walls over long flow lengths with little o.. |
|||
Tensile Strength, Ultimate | 86.2 - 138 MPa | 12500 - 20000 psi | Average value: 110 MPa Grade Count:12 |
Overview of materials for Polyphthalamide (PPA), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Mineral Filled". Each property range of values reported is minimum and maximum values o.. |
|||
Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ISO 62 |
Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC
(discontinued **) Description: Premi-Glas® 1285 VE is a glass reinforced vinyl ester sheet molding compound designed for automotive under the hood applications. Key features and benefits: Designed for compression mo.. |