Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SMC 0390 is a standard low profile SMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surface quality is necessary that can not be achieved with low shrink material. Because of the low shrinkage, tool design is more difficult and the user should take care for proper part demoulding. Typical applications are furniture, telephone boothes, business machines and housings or covers that call for improved surface quality and dimensional stability. Because of this painting may be desired. Paint adhesion of appropriate paint systems is very good. Chrome-plating of punch and cavity surfaces is recommended.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.00020 cm/cm | 0.00020 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 86.0 MPa @Temperature 22.0 °C |
12500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 86.0 MPa @Temperature 22.0 °C |
12500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 1.5 % | 1.5 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 182 MPa @Temperature 22.0 °C |
26400 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Compressive Yield Strength | 90.0 MPa | 13100 psi | ISO 14126 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 4.60 GPa | 667 ksi | in plane |
| Charpy Impact, Notched | 8.20 J/cm² | 39.0 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 170 °C | 338 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 150 °C | 275 - 302 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- LyondellBasell Integrateâ„¢ NP507030 Functionalized Polyolefin
- Kennametal Stellite Stellite® 98M2 with P/M Processing
- Iran Petrochemical (PCC) Arak BL6 HDPE
- IRPC Polimaxx Polene 1111NX TA8 Polypropylene Compound
- American Elements Neodymium Oxide Nanopowder
- Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 63%/120 E-Glass Fiber
- DSM Biomedical CarboSil® 20 80A Thermoplastic Silicone Polycarbonate Polyurethane (TSPCU)
- ExxonMobil LDPE LD 105.30 Low Density Polyethylene Resin
- Dow Nordel® IP 3430 EPDM Hydrocarbon Rubber
- Fainplast Compounds GS 30 Flexible PVC, Injection Molding, Lead Free
Copyright © lookpolymers.com All Rights Reserved