Glastic Laminates/Shapes SG-200 High Strength/High Temperature Polyester Laminate
| Category | Polymer , Thermoset , Composite SMC , Polyester, TS |
| Manufacturer | Glastic |
| Trade Name | Laminates/Shapes |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Glastic Laminates/Shapes SG-200 High Strength/High Temperature Polyester Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Glastic Corporation.NEMA GPO-1. A superior replacement for epoxy-bonded mica in layer insulation applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Yield Strength | 200 MPa | 29000 psi | ASTM D790 |
| Compressive Yield Strength | 248 MPa | 36000 psi | ASTM D695 |
| Shear Strength | 77.0 MPa | 11200 psi | ASTM D732 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | NEMA temperature |
| UL RTI, Electrical | 210 °C | 410 °F | UL 746B |
| UL RTI, Mechanical with Impact | 210 °C | 410 °F | UL 746B |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 21.8 % | 21.8 % | ASTM D2862 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.45e+14 ohm | 1.45e+14 ohm | Insulation Resistance, ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D150 |
| 4.6 @Frequency 60 Hz |
4.6 @Frequency 60 Hz |
ASTM D150 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | Perpendicular, Short-term, in air; ASTM D149 |
| Dissipation Factor | 0.013 @Frequency 1e+6 Hz |
0.013 @Frequency 1e+6 Hz |
ASTM D150 |
| 0.037 @Frequency 60 Hz |
0.037 @Frequency 60 Hz |
ASTM D150 | |
| Arc Resistance | 180 sec | 180 sec | Post-cured, ASTM D495 |
| Comparative Tracking Index | >= 500 V | >= 500 V | UL746A |
| Hot Wire Ignition, HWI | 39 sec | 39 sec | 0.058 in, UL746A |
| High Amp Arc Ignition, HAI | 200 arcs | 200 arcs | UL746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 mm/min | 0.000 in/min | UL746A |
Users viewing this material also viewed the following:
- PolyOne FireCon™ CPE 30-11 REV 2 Polyethylene, Chlorinated (CPE)
- Kolon DIAMAT® EG
- Kolon ELLAS K-475A Ester Based Thermoplastic Polyurethane
- Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI)
- Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N220 (ISAF) Filler
- Wellman Wellamid® GF1662-GY1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66/6
- ExxonMobil 120 Exxon Aviation Oil EE Series
- Asahi Kasei Tenac® 5010 Homopolymer Acetal Resin
- AorTech Biomaterials Elast-Eon™ E2A Biomedical Polyurethane Pellets
Copyright © lookpolymers.com All Rights Reserved