Owens Corning Glass Fiber Reinforced Polyester (Spray-up/Lay-up), 30 wt.% glass
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS |
| Manufacturer | Owens Corning |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Owens Corning Glass Fiber Reinforced Polyester (Spray-up/Lay-up), 30 wt.% glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, Owens Corning.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 hrs.; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 50 | 50 | |
| Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| Modulus of Elasticity | 7.00 GPa | 1020 ksi | ASTM D638 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 5.20 GPa | 754 ksi | ASTM D790 |
| Compressive Strength | 150 MPa | 21800 psi | ASTM D695 |
| Izod Impact, Notched | 7.50 J/cm | 14.1 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.6 µm/m-°C @Temperature 20.0 °C |
12.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Specific Heat Capacity | 1.30 J/g-°C | 0.310 BTU/lb-°F | |
| Thermal Conductivity | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 204 °C | >= 400 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 9.84 kV/mm | 250 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 66-33GF 33% Glass Fiber Filled Nylon 66 for Injection Molding
- Pau Tai UNISTAB MS-169 Solid Complex Stabilizer
- Fiberfil® J-60/20/E8 Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
- MarkeTech Gallium Arsenide Semiconductor Wafer, Semi-Insulating Undoped, LEC Grown
- Solvay Chemicals Barium carbonate granular
- Covestro Baydur® STR/F-375 Polyurethane Composite SRIM Foam, 20% Glass Filled, MDI-based 2-Component Liquid System
- CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Conditioned
- Arkema Group OREVAC® 18350 Grafted Maleic Anhydride Polyethylene
- AKG Polymers Vision PP PPC SK3005 Polypropylene Copolymer Compound
- Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, aged 10 hours at 649°C (1200°F)
Copyright © lookpolymers.com All Rights Reserved