Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC  (discontinued **)

Category Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset , Vinyl Ester , Vinyl Ester Sheet Molding Compound
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Premi-Glas® 1285VE 1285 VE Glass Reinforced Vinyl Ester SMC  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Premi-Glas® 1285 VE is a glass reinforced vinyl ester sheet molding compound designed for automotive under the hood applications. Key features and benefits: Designed for compression molding for optimal strength on large-span coversExcellent resistance to automotive chemicals and fluids, and to salt sprayReplaces cast metals for reduced Noise, Vibration and Harshness, plus molded-in colorMeets the requirements of GMP.UP.018Excellent thermal properties and elevated temperature modulus retentionMarket: Composite PowerTrainInformation provided by Premix.
Physical Properties Metric English Comments
Specific Gravity 1.80 g/cc
1.80 g/cc
ASTM D792
Water Absorption 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage 0.00026 cm/cm
0.00026 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 86.2 MPa
12500 psi
ISO 62
58.6 MPa

@Temperature 150 °C
8500 psi

@Temperature 302 °F
ISO 62
Tensile Modulus 15.2 GPa
2200 ksi
tangent; ISO 527
8.27 GPa

@Temperature 150 °C
1200 ksi

@Temperature 302 °F
ISO 527
Flexural Strength 176 MPa
25500 psi
ISO 178
121 MPa

@Temperature 150 °C
17500 psi

@Temperature 302 °F
ISO 178
Flexural Modulus 6.21 GPa

@Thickness 2.50 mm,
Temperature 150 °C
900 ksi

@Thickness 0.0984 in,
Temperature 302 °F
Secant; ISO 178
8.27 GPa

@Thickness 2.50 mm,
Temperature 22.0 °C
1200 ksi

@Thickness 0.0984 in,
Temperature 71.6 °F
Secant; ISO 178
8.27 GPa

@Thickness 0.500 mm,
Temperature 150 °C
1200 ksi

@Thickness 0.0197 in,
Temperature 302 °F
Secant; ISO 178
11.7 GPa

@Thickness 0.500 mm,
Temperature 22.0 °C
1700 ksi

@Thickness 0.0197 in,
Temperature 71.6 °F
Secant; ISO 178
Izod Impact, Unnotched 12.8 J/cm
24.0 ft-lb/in
ASTM D4812
Impact 0.23
0.23
(in) High Speed Impact (Deflection Max Load); ISO 6603-2
517
517
(lb) High Speed Impact (Impact Max Load); ISO 6603-2
Impact Test 6.91 J
5.10 ft-lb
High Speed Impact (Energy Max Load); ISO 6603-2
12.6 J
9.30 ft-lb
High Speed Impact (Total Energy); ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear 27.0 µm/m-°C

@Temperature 20.0 °C
15.0 µin/in-°F

@Temperature 68.0 °F
Z-direction; ASTM D696
CTE, linear, Transverse to Flow 18.0 µm/m-°C

@Temperature 20.0 °C
10.0 µin/in-°F

@Temperature 68.0 °F
XY-direction; ASTM D696
Thermal Conductivity 0.550 W/m-K
3.82 BTU-in/hr-ft²-°F
ASTM 1530-93
Glass Transition Temp, Tg 188 °C
370 °F
ISO 6721 DMS