BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 7423-2 NF3001 is an impact modified, 13% glass reinforced, heat stabilized injection molding PA6/6.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
dry; ISO 1183
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 86.0 MPa
12500 psi
5mm/min; ISO 527
Elongation at Break 10 %
10 %
5mm/min; ISO 527
Tensile Modulus 4.00 GPa
580 ksi
1mm/min; ISO 527
Flexural Modulus 3.50 GPa
508 ksi
ISO Data
Izod Impact, Notched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
ISO Test
Charpy Impact Unnotched 8.30 J/cm²
39.5 ft-lb/in²
ISO 179
8.10 J/cm²

@Temperature -30.0 °C
 38.5 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
ISO 179
0.500 J/cm²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Thermal Properties Metric English Comments
Melting Point 257 °C
495 °F
10 K/min
257 °C
495 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified Yes
Primary Processing Technique Injection Molding