Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 45.0 - 160 MPa @Temperature -50.0 - 250 °C |
6530 - 23200 psi @Temperature -58.0 - 482 °F |
Average value: 101 MPa Grade Count:1 |
Overview of materials for Polyaryletherketone (PAEK), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Carbon Fiber Filled". Each property range of values reported is minimum and .. |
|||
Tensile Strength, Ultimate | 34.5 - 160 MPa | 5000 - 23200 psi | Average value: 75.2 MPa Grade Count:26 |
Overview of materials for Acetal Homopolymer, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Glass Fiber Reinforced". Each property range of values reported is minimum and maxim.. |
|||
Tensile Strength, Ultimate | 88.0 - 160 MPa | 12800 - 23200 psi | Average value: 124 MPa Grade Count:14 |
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an.. |
|||
Tensile Strength, Ultimate | 0.414 - 160 MPa | 60.0 - 23200 psi | Average value: 7.11 MPa Grade Count:508 |
Overview of materials for Silicone, Molded, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Silicone, Molded, Glass Fiber Filled". Each property range of values reported is minimum and maximum val.. |
|||
Tensile Strength, Ultimate | 100 - 160 MPa @Temperature 60.0 - 150 °C |
14500 - 23200 psi @Temperature 140 - 302 °F |
Average value: 131 MPa Grade Count:1 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | 26.2 - 160 MPa | 3800 - 23200 psi | Average value: 121 MPa Grade Count:41 |
Overview of materials for Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled". Each property range of values reported is minimum.. |
|||
Tensile Strength, Ultimate | 40.0 - 160 MPa @Strain 1.00 - 9.00 % |
5800 - 23200 psi @Strain 1.00 - 9.00 % |
Average value: 104 MPa Grade Count:1 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Tensile Strength, Ultimate | 40.0 - 160 MPa @Temperature 60.0 - 150 °C |
5800 - 23200 psi @Temperature 140 - 302 °F |
Average value: 104 MPa Grade Count:1 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Tensile Strength, Ultimate | 150 - 160 MPa @Temperature 80.0 - 80.0 °C |
21800 - 23200 psi @Temperature 176 - 176 °F |
Average value: 155 MPa Grade Count:2 |
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl.. |
|||
Tensile Strength, Ultimate | 30.0 - 160 MPa @Temperature -40.0 - 150 °C |
4350 - 23200 psi @Temperature -40.0 - 302 °F |
Average value: 66.6 MPa Grade Count:7 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 44.8 - 160 MPa | 6500 - 23200 psi | Average value: 87.1 MPa Grade Count:21 |
Overview of materials for Nylon 6, MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropria.. |