Overview of materials for Silicone, Molded, Glass Fiber Filled

Category Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Silicone, Molded, Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Silicone, Molded, Glass Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.06 - 3.80 g/cc
0.0383 - 0.137 lb/in³
Average value: 1.42 g/cc Grade Count:323
Water Absorption 0.0200 - 0.450 %
0.0200 - 0.450 %
Average value: 0.171 % Grade Count:9
0.240 - 0.240 %

@Temperature 50.0 - 50.0 °C
0.240 - 0.240 %

@Temperature 122 - 122 °F
Average value: 0.240 % Grade Count:1
0.240 - 0.240 %

@Time 173000 - 173000 sec
0.240 - 0.240 %

@Time 48.0 - 48.0 hour
Average value: 0.240 % Grade Count:1
Thickness 12.7 - 25400 microns
0.500 - 1000 mil
Average value: 316 microns Grade Count:504
Linear Mold Shrinkage 0.00100 - 0.00800 cm/cm
0.00100 - 0.00800 in/in
Average value: 0.00319 cm/cm Grade Count:7
Outgassing - Total Mass Loss 0.100 - 1.07 %
0.100 - 1.07 %
Average value: 0.563 % Grade Count:6
0.100 - 0.340 %

@Temperature 218 - 218 °C
0.100 - 0.340 %

@Temperature 425 - 425 °F
Average value: 0.220 % Grade Count:1
0.100 - 0.340 %

@Time 7200 - 7200 sec
0.100 - 0.340 %

@Time 2.00 - 2.00 hour
Average value: 0.220 % Grade Count:1
Mechanical Properties Metric English Comments
Hardness, Rockwell M 75.0 - 90.0
75.0 - 90.0
Average value: 86.3 Grade Count:4
Hardness, Shore A 18.0 - 92.0
18.0 - 92.0
Average value: 53.0 Grade Count:499
Tensile Strength, Ultimate 0.414 - 160 MPa
60.0 - 23200 psi
Average value: 7.11 MPa Grade Count:508
Tensile Strength, Yield 1.38 - 62.1 MPa
200 - 9000 psi
Average value: 23.2 MPa Grade Count:13
Elongation at Break 5.00 - 1150 %
5.00 - 1150 %
Average value: 394 % Grade Count:496
Elongation at Yield 31.0 - 38.0 %
31.0 - 38.0 %
Average value: 35.7 % Grade Count:3
Modulus of Elasticity 0.00159 - 14.0 GPa
0.230 - 2030 ksi
Average value: 2.19 GPa Grade Count:16
Flexural Yield Strength 30.0 - 180 MPa
4350 - 26100 psi
Average value: 86.8 MPa Grade Count:14
Flexural Modulus 8.00 - 16.0 GPa
1160 - 2320 ksi
Average value: 12.5 GPa Grade Count:9
Compressive Yield Strength 40.0 - 331 MPa
5800 - 48000 psi
Average value: 159 MPa Grade Count:13
Poissons Ratio 0.500
0.500
Average value: 0.500 Grade Count:27
Shear Modulus 0.0000689 - 1.83 GPa
0.0100 - 265 ksi
Average value: 0.208 GPa Grade Count:24
Shear Strength 0.965 - 20.0 MPa
140 - 2900 psi
Average value: 4.48 MPa Grade Count:31
Adhesive Bond Strength 0.0103 - 150 MPa
1.50 - 21800 psi
Average value: 3.62 MPa Grade Count:40
Izod Impact, Notched 0.200 - 3.93 J/cm
0.375 - 7.36 ft-lb/in
Average value: 1.34 J/cm Grade Count:5
Charpy Impact Unnotched 0.400 - 2.50 J/cm²
1.90 - 11.9 ft-lb/in²
Average value: 1.38 J/cm² Grade Count:4
Tear Strength 4.91 - 51.9 kN/m
28.0 - 296 pli
Average value: 17.4 kN/m Grade Count:181
Peel Strength 0.0877 - 7.05 kN/m
0.500 - 40.2 pli
Average value: 1.46 kN/m Grade Count:353
Compression Set 25.0 - 49.0 %
25.0 - 49.0 %
Average value: 31.8 % Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 11.0 - 280 µm/m-°C
6.11 - 156 µin/in-°F
Average value: 90.4 µm/m-°C Grade Count:29
20.0 - 40.0 µm/m-°C

@Temperature 50.0 - 150 °C
11.1 - 22.2 µin/in-°F

@Temperature 122 - 302 °F
Average value: 30.0 µm/m-°C Grade Count:2
CTE, linear, Transverse to Flow 20.0 - 40.0 µm/m-°C
11.1 - 22.2 µin/in-°F
Average value: 33.3 µm/m-°C Grade Count:3
Specific Heat Capacity 0.320 - 1.14 J/g-°C
0.0765 - 0.272 BTU/lb-°F
Average value: 0.864 J/g-°C Grade Count:15
0.820 - 0.920 J/g-°C

@Temperature 100 - 100 °C
0.196 - 0.220 BTU/lb-°F

@Temperature 212 - 212 °F
Average value: 0.842 J/g-°C Grade Count:13
Thermal Conductivity 0.0600 - 32.0 W/m-K
0.416 - 222 BTU-in/hr-ft²-°F
Average value: 1.64 W/m-K Grade Count:35
1.00 - 3.00 W/m-K

@Temperature 50.0 - 100 °C
6.94 - 20.8 BTU-in/hr-ft²-°F

@Temperature 122 - 212 °F
Average value: 1.94 W/m-K Grade Count:14
1.50 - 4.69 W/m-K

@Temperature 50.0 - 50.0 °C
10.4 - 32.5 BTU-in/hr-ft²-°F

@Temperature 122 - 122 °F
Average value: 1.94 W/m-K Grade Count:4
1.50 - 4.69 W/m-K

@Pressure 30.0 - 30.0 MPa
10.4 - 32.5 BTU-in/hr-ft²-°F

@Pressure 4350 - 4350 psi
Average value: 1.94 W/m-K Grade Count:4
Maximum Service Temperature, Air 95.6 - 300 °C
204 - 572 °F
Average value: 228 °C Grade Count:415
Maximum Service Temperature, Inert 149 - 232 °C
300 - 450 °F
Average value: 226 °C Grade Count:92
Deflection Temperature at 1.8 MPa (264 psi) 200 - 282 °C
392 - 540 °F
Average value: 259 °C Grade Count:7
Minimum Service Temperature, Air -136 - -40.0 °C
-212 - -40.0 °F
Average value: -58.5 °C Grade Count:491
Glass Transition Temp, Tg -120 - 118 °C
-184 - 244 °F
Average value: -104 °C Grade Count:29
UL RTI, Electrical 150 - 220 °C
302 - 428 °F
Average value: 211 °C Grade Count:127
UL RTI, Mechanical without Impact 150 - 220 °C
302 - 428 °F
Average value: 203 °C Grade Count:127
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:144
HB - HB

@Temperature 200 - 220 °C
HB - HB

@Temperature 392 - 428 °F
Grade Count:15
Electrical Properties Metric English Comments
Electrical Resistivity 0.0500 - 1.00e+16 ohm-cm
0.0500 - 1.00e+16 ohm-cm
Average value: 8.93e+14 ohm-cm Grade Count:7
Insulation Resistance 1.00e+8 - 1.00e+11 ohm
1.00e+8 - 1.00e+11 ohm
Average value: 1.94e+10 ohm Grade Count:6
Dielectric Constant 3.20 - 6.91
3.20 - 6.91
Average value: 4.75 Grade Count:35
Dielectric Strength 1.60 - 59.1 kV/mm
40.6 - 1500 kV/in
Average value: 21.3 kV/mm Grade Count:455
Dielectric Breakdown >= 25000 V

@Temperature 90.0 - 90.0 °C
>= 25000 V

@Temperature 194 - 194 °F
Average value: 31500 V Grade Count:2
>= 30000 V

@Temperature 90.0 - 90.0 °C
>= 30000 V

@Temperature 194 - 194 °F
Average value: 31500 V Grade Count:2
>= 30000 V

@Time 20.0 - 60.0 sec
>= 30000 V

@Time 0.00556 - 0.0167 hour
Average value: 31500 V Grade Count:2
Dissipation Factor 0.00150 - 0.0700
0.00150 - 0.0700
Average value: 0.0109 Grade Count:35
Arc Resistance 180 - 240 sec
180 - 240 sec
Average value: 208 sec Grade Count:8
Comparative Tracking Index 300 - 450 V
300 - 450 V
Average value: 390 V Grade Count:5