Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Nylon 6, 30 wt.% glass Nylons, as a group, are inert to most organic solvents. They resist alkalis and salt solutions and they are attacked by strong mineral acids and oxidizing agents. Data provided by the manufacturer,.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® GR40 HS 40% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron GR40 HS is a heat stabilized 40% glass reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stabil.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5 mm/min; ISO 527-2/1A |
Global GP-5180-30 PET 30% Glass Reinforced PET Polyester
(discontinued **) Information provided by Global Polymers Corporation. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AFA-6133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded
&nbs AMODEL AFA-6133 V0 is a 33% glass-fiber reinforced grade of polyphthalamide (PPA) resin that was developed specifically for connector applications requiring compatibility with both "infrared" and "v.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® R-4-200BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-200BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound developed to provide high strength, fast cycles, and low maintenance mol.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM data at 5 mm/min. |
BASF Capron® 8232G 25% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8232G is a 25% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under l.. |
|||
Tensile Strength, Ultimate | >= 170 MPa | >= 24700 psi | |
MetalTek MTEK 76-6-18 HI LEAD Cast UNS C94100 Bearing Bronze Popular alloy with score resistance, structural uniformity, shear properties, compressive strength and low cost.Applications: Bearings, bushings, sleeves, liners, piston rings, hydraulic partsInform.. |
|||
Tensile Strength, Ultimate | >= 170 MPa | >= 24700 psi | |
MetalTek MTEK 79-6-15 HI LEAD Cast UNS C93900 Bearing Bronze Popular alloy with score resistance, structural uniformity, shear properties, compressive strength and low cost.Applications: Bearings, bushings, sleeves, liners, piston rings, hydraulic partsInform.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | |
ICE Al2O3 94 Data provided by the manufacturer, International Ceramic Engineering. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | |
ICE Al2O3 99.5 Data provided by the manufacturer, International Ceramic Engineering. |
|||
Tensile Strength, Ultimate | 170 - 340 MPa | 24700 - 49300 psi | |
Materion Brush 1915â„¢ Annealed Temper Wire Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: as suppliedBrush 1915â„¢ is Brush Wellman's new heat-treatable leaded copper alloy. Engineered spe.. |
|||
Tensile Strength, Ultimate | 170 MPa @Temperature 980 °C |
24700 psi @Temperature 1800 °F |
|
Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | |
Sapco 95% Aluminum Oxide Information provided by Sapco. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASMT D638 |
Toyobo TS201 PPS, Glass Fiber/Mineral Reinforced Key Feature: Standard high stiffness - used for metal replacementHigh performance injection-molding resin created from crystalline polyphenylene sulfide, using a special formulation technology devel.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM EcoPaXX® Q-KG6 PA410-GF30 % Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1013G30 1 NA PA6-GF30 30% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1013GH30 1 NA/BK701 PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17) 30% Glass Reinforced, Flame Retardant |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Stanyl® 46SF5030 PA46-GF30 FR(17) 30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TW271B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | cond; ISO 527-1/-2 |
DSM EcoPaXX® Q-HG10 PA410-GF50 50% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM EcoPaXX® Q-HG6 PA410-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 |
BASF Petra® 140 BK-112 45% Glass Filled PET Petra 140 BK-112 is a 45% glass reinforced, pigmented black, polyethylene terephthalate (PET) injection molding compound offering an increased level of strength, stiffness, high temperature performa.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 |
BASF Ultramid® 8233G HS BK-102 33% Glass Filled PA6 (Dry) Ultramid 8233G HS BK-102 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and d.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 |
BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry) Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat
cushion .. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 3021GH30 BK629 PA66-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TQ261F5 PA46-GF25 25% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® GR40 40% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron GR40 is a 40% glass reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is also ava.. |
|||
Tensile Strength, Ultimate | 170 MPa @Thickness 5.00 mm, Temperature 200 °C |
24700 psi @Thickness 0.197 in, Temperature 392 °F |
Typical L-T Direction |
Aleris HOGAL 5558 Aluminum 5026 H14/H34 HOGAL 5558 is produced according to EN AW-5026.Information provided by Aleris. |