Haynes 263® alloy, cold rolled sheet, solution treated and aged

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 263® alloy, cold rolled sheet, solution treated and aged.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excellent forming and welding characteristics. Applications include aircraft and land-based turbine engine applications, low-temperature combustors, transition liners, and some ring components.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.36 g/cc
0.302 lb/in³
a RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1050 MPa
152000 psi
88.0 MPa

@Temperature 1095 °C
 12800 psi

@Temperature 2003 °F
170 MPa

@Temperature 980 °C
 24700 psi

@Temperature 1800 °F
350 MPa

@Temperature 870 °C
 50800 psi

@Temperature 1600 °F
725 MPa

@Temperature 760 °C
 105000 psi

@Temperature 1400 °F
835 MPa

@Temperature 650 °C
 121000 psi

@Temperature 1200 °F
855 MPa

@Temperature 540 °C
 124000 psi

@Temperature 1000 °F
Tensile Strength, Yield 635 MPa

@Strain 0.200 %
 92100 psi

@Strain 0.200 %
37.0 MPa

@Strain 0.200 %,
Temperature 1095 °C
 5370 psi

@Strain 0.200 %,
Temperature 2003 °F
87.0 MPa

@Strain 0.200 %,
Temperature 980 °C
 12600 psi

@Strain 0.200 %,
Temperature 1800 °F
220 MPa

@Strain 0.200 %,
Temperature 870 °C
 31900 psi

@Strain 0.200 %,
Temperature 1600 °F
515 MPa

@Strain 0.200 %,
Temperature 760 °C
 74700 psi

@Strain 0.200 %,
Temperature 1400 °F
525 MPa

@Strain 0.200 %,
Temperature 650 °C
 76100 psi

@Strain 0.200 %,
Temperature 1200 °F
540 MPa

@Strain 0.200 %,
Temperature 540 °C
 78300 psi

@Strain 0.200 %,
Temperature 1000 °F
Elongation at Break 35.7 %
35.7 %
in 51 mm
33.1 %

@Temperature 760 °C
 33.1 %

@Temperature 1400 °F
 in 51 mm
35.6 %

@Temperature 650 °C
 35.6 %

@Temperature 1200 °F
 in 51 mm
38.6 %

@Temperature 540 °C
 38.6 %

@Temperature 1000 °F
 in 51 mm
54.7 %

@Temperature 870 °C
 54.7 %

@Temperature 1600 °F
 in 51 mm
58.7 %

@Temperature 1095 °C
 58.7 %

@Temperature 2003 °F
 in 51 mm
71.8 %

@Temperature 980 °C
 71.8 %

@Temperature 1800 °F
 in 51 mm
Modulus of Elasticity 221 GPa
32100 ksi
RT
143 GPa

@Temperature 1000 °C
 20700 ksi

@Temperature 1830 °F
154 GPa

@Temperature 900 °C
 22300 ksi

@Temperature 1650 °F
166 GPa

@Temperature 800 °C
 24100 ksi

@Temperature 1470 °F
176 GPa

@Temperature 700 °C
 25500 ksi

@Temperature 1290 °F
185 GPa

@Temperature 600 °C
 26800 ksi

@Temperature 1110 °F
192 GPa

@Temperature 500 °C
 27800 ksi

@Temperature 932 °F
198 GPa

@Temperature 400 °C
 28700 ksi

@Temperature 752 °F
205 GPa

@Temperature 300 °C
 29700 ksi

@Temperature 572 °F
212 GPa

@Temperature 200 °C
 30700 ksi

@Temperature 392 °F
219 GPa

@Temperature 100 °C
 31800 ksi

@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 11.1 µm/m-°C

@Temperature 25.0 - 100 °C
 6.17 µin/in-°F

@Temperature 77.0 - 212 °F
12.1 µm/m-°C

@Temperature 25.0 - 200 °C
 6.72 µin/in-°F

@Temperature 77.0 - 392 °F
12.7 µm/m-°C

@Temperature 25.0 - 300 °C
 7.06 µin/in-°F

@Temperature 77.0 - 572 °F
12.8 µm/m-°C

@Temperature 25.0 - 400 °C
 7.11 µin/in-°F

@Temperature 77.0 - 752 °F
13.6 µm/m-°C

@Temperature 25.0 - 500 °C
 7.56 µin/in-°F

@Temperature 77.0 - 932 °F
18.1 µm/m-°C

@Temperature 1000 °C
 10.1 µin/in-°F

@Temperature 1830 °F
Thermal Conductivity 11.7 W/m-K
81.2 BTU-in/hr-ft²-°F
RT
13.0 W/m-K

@Temperature 100 °C
 90.2 BTU-in/hr-ft²-°F

@Temperature 212 °F
14.7 W/m-K

@Temperature 200 °C
 102 BTU-in/hr-ft²-°F

@Temperature 392 °F
16.3 W/m-K

@Temperature 300 °C
 113 BTU-in/hr-ft²-°F

@Temperature 572 °F
18.0 W/m-K

@Temperature 400 °C
 125 BTU-in/hr-ft²-°F

@Temperature 752 °F
19.7 W/m-K

@Temperature 500 °C
 137 BTU-in/hr-ft²-°F

@Temperature 932 °F
21.4 W/m-K

@Temperature 600 °C
 149 BTU-in/hr-ft²-°F

@Temperature 1110 °F
23.0 W/m-K

@Temperature 700 °C
 160 BTU-in/hr-ft²-°F

@Temperature 1290 °F
24.7 W/m-K

@Temperature 800 °C
 171 BTU-in/hr-ft²-°F

@Temperature 1470 °F
26.8 W/m-K

@Temperature 900 °C
 186 BTU-in/hr-ft²-°F

@Temperature 1650 °F
28.5 W/m-K

@Temperature 1000 °C
 198 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Melting Point 1300 - 1355 °C
2370 - 2471 °F
Solidus 1300 °C
2370 °F
Liquidus 1355 °C
2471 °F
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.60 %
<= 0.60 %
Carbon, C 0.060 %
0.060 %
Chromium, Cr 20 %
20 %
Cobalt, Co 20 %
20 %
Copper, Cu <= 0.20 %
<= 0.20 %
Iron, Fe <= 0.70 %
<= 0.70 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000115 ohm-cm
0.000115 ohm-cm
RT
0.000116 ohm-cm

@Temperature 100 °C
 0.000116 ohm-cm

@Temperature 212 °F
0.000118 ohm-cm

@Temperature 200 °C
 0.000118 ohm-cm

@Temperature 392 °F
0.000120 ohm-cm

@Temperature 300 °C
 0.000120 ohm-cm

@Temperature 572 °F
0.000122 ohm-cm

@Temperature 400 °C
 0.000122 ohm-cm

@Temperature 752 °F
0.000124 ohm-cm

@Temperature 500 °C
 0.000124 ohm-cm

@Temperature 932 °F
0.000124 ohm-cm

@Temperature 900 °C
 0.000124 ohm-cm

@Temperature 1650 °F
0.000124 ohm-cm

@Temperature 1000 °C
 0.000124 ohm-cm

@Temperature 1830 °F
0.000125 ohm-cm

@Temperature 800 °C
 0.000125 ohm-cm

@Temperature 1470 °F
0.000126 ohm-cm

@Temperature 600 °C
 0.000126 ohm-cm

@Temperature 1110 °F
0.000126 ohm-cm

@Temperature 700 °C
 0.000126 ohm-cm

@Temperature 1290 °F