Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL32 PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL32 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Lendell Parapet EH-1000 PMMA, Extrusion |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN131 General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN1322VO Flame Retardant Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP3200B(W) PA66+MF20%, General Purpose Feature: Injection Molding, PA6+MF20%, General PurposeApplication: E&E (Rice Cooker Housing)Information provided by LG Chemical |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN333HS Heat Resistant Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOS GP2206F ABS+GF20%, Flame Retardant Feature: Injection Molding, ABS+GF20%, Flame RetardantApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7, 65997-17-3, 88497-56-7 and 1309-64-4Information provided b.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Global 120-PC-Natural Acrylonitrile Styrene, General Purpose Grade Description-transparent, natural, medium impact resistance, high hardness, high heat resistance, good chemical resistanceApplications-automotive, electrical parts, household goodsInformation provide.. |
|||
Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
LG Chemical LUPOY GN1000FA PC, Halogen Free, Flame Retardant, Transparency Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 181028-79-5Information provided by .. |
|||
Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUPOY GN2101FC PC+GF10%, Halogen Free, Flame Retardant, Heat Resistance Description: Injection Molding, PC+GF10%, Halogen Free Flame RetardanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemi.. |
|||
Flexural Yield Strength | 118 MPa @Temperature 23.0 °C |
17100 psi @Temperature 73.4 °F |
ASTM D790 |
IRPC Polimaxx Polene 120PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
Flexural Yield Strength | 118 MPa @Temperature 23.0 °C |
17100 psi @Temperature 73.4 °F |
ASTM D790 |
IRPC Polimaxx Polene 121PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | DIN 53455; ASTM D790 |
Kolon KOPA® KN133MT40 M/F Reinforced Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical 80HF SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical |
|||
Flexural Yield Strength | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical 80HFICELLHK SAN, High Transparency, Heat Resistance, Chemical Resistance Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Refrigerator Sleeves, MiscellaneousCAS No. 9003-54-7Information provided by LG Chemical |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Samyang Tribit® 1500G15K PBT, Reinforced Impact Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1500G15K is a reinforced, impact grade.Appl.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Samyang Tribit® 1551GN15 PBT, Reinforced Flame Retardancy Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1551GN15 is a reinforced, flame retardant g.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® P305G30 PP, 30% Glass Filled Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Asia Pacific) Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Noryl GTX APS8740 PPE+PPS (Europe-Africa-Middle East) Noryl* APS8740 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be e.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX EXNX0080 PPE+PPS (Europe-Africa-Middle East) Noryl APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
PlastxWorld CEVIAN® SKG20 20% GF ABS Glass fiber reinforced, heat resistant and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by Plast.. |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Cheng Yu Plastic N6C1 Nylon 6, 10% Mineral Reinforced |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Cheng Yu Plastic PP238G3 Polypropylene, 30% Glass Fiber |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Cheng Yu Plastic A702G15 ABS 15% Glass Fiber Reinforced |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
Cheng Yu Plastic FRCV100 Flame Retardant Nylon 66, 10% Mineral Reinforced |
|||
Flexural Yield Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL32XXP PC (Europe-Africa-Middle East) LNP* Lubricomp* DFL32XXP is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. |