- Samyang Tribit® 1551GN15 PBT, Reinforced Flame Retardancy
Samyang Tribit® 1551GN15 PBT, Reinforced Flame Retardancy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Samyang |
| Trade Name | Tribit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tribit® 1551GN15 PBT, Reinforced Flame Retardancy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1551GN15 is a reinforced, flame retardant grade.Applications: Connectors (insulation characteristics)Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm | 0.0020 - 0.012 in/in | ASTM D955 |
| Melt Flow | 57 g/10 min @Load 2.16 kg, Temperature 250 °C |
57 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 88.3 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 118 MPa | 17100 psi | ASTM D790 |
| Flexural Modulus | 5.39 GPa | 782 ksi | ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm @Thickness 3.17 mm |
0.551 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 | 3.1 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 | 0.020 | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Cookson Group Plaskon® SMT-B-1RC (146.403) Epoxy Molding Compound for PBGAs (discontinued **)
- Lord Adhesives Metech 3504 Palladium Silver Conductor Composition
- Ineos N02J-00 Polypropylene Impact Copolymer
- Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Conditioned
- 3M 6035PC 12032 Polyurethane Foam Tape (15 lb./ft3 (239 kg/m3) Series)
- Asahi Kasei Leona® FR370 Nylon 66
- ATI Allegheny Ludlum Stainless Steel Type 201, 30% Cold Work (UNS S20100)
- Borealis MB350WG Polypropylene Compound, Mineral Filled
- Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure
Copyright © lookpolymers.com All Rights Reserved