- Polymer Property : Flexural Yield Strength = 98.0 MPa
Polymer Property : Flexural Yield Strength = 98.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Cycoloy® CS9610 PC+ABS (Europe-Africa-Middle East) Cycoloy* CS9610 is a FR PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering optimum mechanical & impact balance and excellent flammability and low smoke behavior... |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Cycoloy® FXC630ME PC+ABS (Europe-Africa-Middle East) PC+ABS, of non-chlorinated & non brominated flame retardant with metallic or pearlescent appearance. MAGIX color package may affect performance.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® 915AU PC LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® BM5225X PC (Asia Pacific) BM5225X resin is a mineral filled grade featuring of high modulus, good flow and ductility, low warpage. It is of non-Br & non-Cl flame retardant systems intended to meet thin wall flame resistance .. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL4019 PC (Europe-Africa-Middle East) Lexan* EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers im.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® FXG154 PC FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.This data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1034 PC Copolymer 7 MFR LEXAN HFD Copolymer UV-stabilized, available in transparent colors only |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1034 PC Copolymer (Europe-Africa-Middle East) 7 MFR LEXAN HFD Copolymer UV-stabilized, available in transparent colors only |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Europe-Africa-Middle East) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1413 PC Copolymer 11 MFR LEXAN High Flow Ductile Copolymer |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HP2EU PC (Europe-Africa-Middle East) Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mol.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HP2REU PC (Europe-Africa-Middle East) Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains a h.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® LUX7189 PC (Europe-Africa-Middle East) Lexan* LUX7189 is an injection moldable, high light reflectance FR grade. Contains non-brominated, non-chlorinated flame retardant systems. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® LUX9130T PC COPOLYMER (Asia Pacific) LUX9130T Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm / 5VA rating at 6.0mm and is U.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® ML6819 PC (Asia Pacific) Medium flow, UV stabilised, high impact grade of polycarbonate.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Cycoloy® C7230P PC+ABS (Asia Pacific) Cycoloy* C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® EXRL0683 PC Copolymer 11 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | ASTM D790 |
| Asahi Kasei Tenac® FA405 Acetal Homopolymer, Low Friction Grade
(discontinued **) Contains fluoropolymer and lubricant; excellent friction and wear on plastics.Applications: Bearings for printers, cams, gears.This product is not a part of the standard product line dated 2003. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | DIN 53452; ASTM D790 |
| Kolon Kopa® KN173HI Nylon 6 Resin KOPA is widely used in the automobile and industrial parts.General KOPA N-6 Features: Good mechanical properties, Extreme toughness, Outstanding self-lubrication and abrasion resistance, Excellent c.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Noryl V01505 PPE+HIPS (Asia Pacific) Noryl* V01505 is a 15% milled fibre reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer Siltem STM1700 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxici.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Xenoy® X4870HH PC+PET (Europe-Africa-Middle East) Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional st.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL N190X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. RTI Elec/Imp/Str 95/80/95. Dielectric strength. Suitable for E/E market applications. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer (Europe-Africa-Middle East) Siltem STM1700 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxici.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX918W PPE+PS+PA (Asia Pacific) High flow NORYL GTX resin for under-the-hood and electrical applications requiring retention of properties under thermal load |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL GTX GTX918WR PPE+PS+PA High flow PPE+PS+PA for under-the-hood and electrical applications. With mold release |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Noryl GTX GTX918WR PPE+PS+PA (Asia Pacific) High flow PPE+PS+PA for under-the-hood and electrical applications. With mold releaseThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® FXG154 PC (Europe-Africa-Middle East) FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.This data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1433 PC Copolymer (Europe-Africa-Middle East) 11 MFR LEXAN High Flow Ductile Copolymer UV stabilized, available in transparent colors only |
|||