SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM STM1700 PEI Copolymer (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Siltem STM1700 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity. It is an amber colored transparent material that can be selfcolored and easily processed on conventional equipment. The material may also have a fit in flexible profiles or injection molded parts.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption at Saturation 0.76 %
0.76 %
ISO 62
Linear Mold Shrinkage, Flow 0.0087 - 0.0092 cm/cm

@Thickness 3.20 mm
 0.0087 - 0.0092 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 7.0 g/10 min

@Load 6.60 kg,
Temperature 295 °C
 7.0 g/10 min

@Load 14.6 lb,
Temperature 563 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
ASTM D2240
Tensile Strength at Break 59.0 MPa
8560 psi
50 mm/min; ISO 527
Tensile Strength, Yield 68.0 MPa
9860 psi
50 mm/min; ISO 527
Elongation at Break 15 %
15 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Flexural Modulus 2.00 GPa
290 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Tear Strength 37.0 kN/m

@Thickness 1.60 mm
 211 pli

@Thickness 0.0630 in
 ISO 34 (Method A)
Taber Abrasion, mg/1000 Cycles 50
50
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
Transformation Temperature, Tg 200 °C
392 °F
DMA
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Vicat Softening Point 180 °C
356 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 UL 94 by SABIC-IP
Oxygen Index 48 %
48 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ASTM D257
Dielectric Constant 3.04

@Frequency 1.00e+6 Hz
 3.04

@Frequency 1.00e+6 Hz
 ASTM D150
3.1

@Frequency 100000 Hz
 3.1

@Frequency 100000 Hz
 ASTM D150
3.13

@Frequency 100 Hz
 3.13

@Frequency 100 Hz
 ASTM D150
Dielectric Strength 16.7 kV/mm

@Thickness 3.20 mm
 424 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
Dissipation Factor 0.0054

@Frequency 1.00e+6 Hz
 0.0054

@Frequency 1.00e+6 Hz
 ASTM D150
0.0061

@Frequency 100000 Hz
 0.0061

@Frequency 100000 Hz
 ASTM D150
0.011

@Frequency 100 Hz
 0.011

@Frequency 100 Hz
 ASTM D150