SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts may form opaque areas in the centre due to slow cooling.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.140 %
0.140 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.16 %
0.16 %
ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0070 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 12.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
12.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
66.0 MPa
9570 psi
50 mm/min; ISO 527
Tensile Strength, Yield 58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
61.0 MPa
8850 psi
50 mm/min; ISO 527
Elongation at Break 120 %
120 %
Type I, 50 mm/min; ASTM D638
134 %
134 %
50 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.37 GPa
344 ksi
1 mm/min; ISO 527
2.47 GPa
358 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.03 GPa
294 ksi
2 mm/min; ISO 178
2.24 GPa
325 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 7.00 J/cm
13.1 ft-lb/in
ASTM D256
1.00 J/cm

@Temperature -30.0 °C
1.87 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 74.0 J

@Temperature 23.0 °C
54.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 67.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 112 °C
234 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
113 °C

@Thickness 3.20 mm
235 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 130 °C
266 °F
Rate B/50; ASTM D1525
130 °C
266 °F
Rate B/50; ISO 306
132 °C
270 °F
Rate B/120; ISO 306