Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
Polimeri Europa Riblene® FL 23 Low Density Polyethylene - Blown Film Extrusion Riblene FL 23 is a low density polyethylene (LDPE) with added slip agent, suitable for blown film extrusion. Riblene FL 23 is characterized by a good balance between processability and mechanical p.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
Polimeri Europa Riblene® FL 24 Low Density Polyethylene - Blown Film Extrusion Riblene FL 24 is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FL 24 is characterized by a good balance between processabilit.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1386 PRE-ELEC PP 1386 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa @Thickness 0.400 mm |
3340 psi @Thickness 0.0157 in |
ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1391 Conductive Thermoplastic Compound PRE-ELEC® PP 1391 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa @Thickness 0.400 mm |
3340 psi @Thickness 0.0157 in |
ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1397 Conductive Thermoplastic Compound PRE-ELEC® PP 1397 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-E.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
NOVA Chemicals Sclair® 19H Homopolymer HDPE Film Resin Features: High stiffnessGood processability Low gel Applications: BlendingCo-extrusionInformation provided by Nova Chemicals |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Petroquimica Triunfo Trithene® TN 7006 LDPE - Coextruded Film The Trithene® TS 7006 resin is a low-density polyethylene (LDPE) with high molecular weight and very good clarity. The unique combination of good processability, bubble stability, gloss, and streng.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Petroquimica Triunfo Trithene® TS 7006 LDPE - Coextruded Film The Trithene TS 7006 resin is a low-density polyethylene (LDPE) with high molecular weight and very good clarity. The unique combination of good processability, bubble stability, gloss, and strength.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Eastman 1830F Polyethylene
(discontinued **) Polyethylene 1830F is a low-density formulation with no slip or antiblock. It is suggested for film applications requiring high clarity, good tear and impact strength, a wide heat sealing range and.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Eastman E6838-922F Polyethylene
(discontinued **) E6838-922F is a low density formulation with medium slip and medium antiblock. Outstanding optical properties make this material an excellent choice for food packaging applications.List of Applicat.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Chevron Phillips HiD® 9605D HDPE Cast Film Resin
(discontinued **) Characteristics: Very Low Gel Levels, Produces Very "Clear" Film, Draws to Thin Gauges, Low Taste and Odor Transfer, Excellent MVTR for a Chill Cast Film, Excellent Processability, Excellent Optical.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Chevron Phillips HiD® 9607D HDPE Cast Film Resin
(discontinued **) Characteristics: Very Low Gel Levels, Produces Very "Clear" Film, Draws to Thin Gauges, Low Taste and Odor Transfer, Excellent MVTR for a Chill Cast Film, Excellent Processability, Excellent Optical.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Chevron Phillips MarFlex® 9607XD HDPE Cast Film Resin
(discontinued **) Characteristics: Very Low Gel Levels, Produces Very "Clear" Film, Draws to Thin Gauges, Low Taste and Odor Transfer, Excellent MVTR for a Chill Cast Film, Excellent Processability, Excellent Optical.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D 882 |
NOVA Chemicals Novapol® PF-0318-E Butene LLDPE Film Resin PF-0318-E complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. It is also biolog.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Huntsman PE1503 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Huntsman PE1504 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
Borealis FA3220 Low Density Polyethylene FA3220 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Unmodified. This grade is developed to give a strong film with balanced shrink properties. Applications FA3220 has bee.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa @Temperature 24.0 °C |
3340 psi @Temperature 75.2 °F |
22mm/min; ISO 527-3 |
Borealis FA3227 Low Density Polyethylene FA3227 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Heat and U/V stabilized. This grade is suitable for building construction film and meets the requirements for heat, al.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | 22mm/min; ISO 527-3 |
Borealis FA5223 Low Density Polyethylene FA5223 is a Low Density Polyethylene for Film Extrusion. Contains antioxidant and antiblock additive. This grade is developed to give strong film for medium duty applications. Applications FA5223.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
Borealis FA5224 Low Density Polyethylene FA5224 is a Low Density Polyethylene for Film Extrusion. Contains Antioxidant, Anti-block and Medium Slip additives. This grade is developed to give strong film for medium duty applications. Appl.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Westlake EF403 Low Density Polyethylene WESTLAKE polyethylene EB403 is a fractional melt low-density formulation suggested for use in clarity shrink applications. This LDPE formula exhibits excellent shrinkability, and has very good optic.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
Total EVA 1040 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1040 VN 4 is made by a high pressure tubular process. Grade for very flexible films with high transparency and good mechanical properties. Contains an antioxidant.Application examples: Thin st.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Chevron Phillips MarFlex® 9607 HDPE Cast Film Resin Characteristics: Very Low Gel Levels, Produces Very "Clear" Film, Draws to Thin Gauges, Low Taste and Odor Transfer, Excellent MVTR for a Chill Cast Film, Excellent Processability, Excellent Optical.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | Calculated from mfr's report of 31 N/cm per ASTM D828 and the typical thickness |
DuPont™ Nomex® E56 Paper, 5 mil Nominal Thickness Nomex® Type E56 is designed for cost critical uses which require lesser amounts of mechanical and electrical strength than other Nomex® grades. It is thermally similar to Nomex® Type 410 but as.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa @Thickness 0.0250 mm |
3340 psi @Thickness 0.000984 in |
ASTM D882 |
Equate EFDC-7050 LLDPE Film Extrusion Resin EFDC-7050 is a linear low-density polyethylene resin for tubular blown film extrusion. Films extruded from EFDC-7050 have good toughness and high tensile strength and puncture resistance. The produc.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM-D882 |
Braskem TN7006 LDPE Blown Film Extrusion Polyethylene TN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination of mechanical, optical, and stiffness properties. TN7006 h.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM-D882 |
Braskem TS7006 LDPE Blown Film Extrusion Polyethylene TS7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a combination of mechanical, optical, and stiffness properties. TS7006 has a l.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM-D882 |
Braskem TU3002 LDPE Blown Film Extrusion Polyethylene TU3002 is a low-density polyethylene (LDPE) with high molecular weight, excellent mechanical properties (dart drop and Elmendorf tear strength), and good processability. These qualities ensure the p.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Eastman D4032-F Polyethylene
(discontinued **) D4032-F is a low density, fractional-melt formulation which contains no slip and medium antiblock. It is designed for film applications requiring exceptional toughness, such as in heavy-duty shippi.. |
|||
Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
Chevron Phillips MarFlex® 9608XD HDPE Film Grade This HDPE is tailored for applications that require:Very low gel levelsVery "clear" filmExcellent drawdownEnhanced stiffnessExcellent WVTR for a chill cast filmExcellent ProcessibilityTypical Cast F.. |