Borealis FA5223 Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Borealis |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Borealis FA5223 Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FA5223 is a Low Density Polyethylene for Film Extrusion. Contains antioxidant and antiblock additive. This grade is developed to give strong film for medium duty applications. Applications FA5223 has been developed especially for applications like heavy-duty sacks, food packaging, shrink film, carrier-bag film, pouches, and general packaging film.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Antiblock Level | 850 ppm | 850 ppm | talc; Borealis Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 500 % | 500 % | ISO 527-3 |
| Tensile Modulus | 0.180 GPa | 26.1 ksi | MD/TD; ASTM D882-A |
| Puncture Energy | 2.00 J | 1.48 ft-lb | 53 N; 40µm sample; ASTM D5748 |
| Coefficient of Friction | 0.80 | 0.80 | Dynamic; ISO 8295 |
| Elmendorf Tear Strength, MD | 10.19 g/micron | 258.8 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 5.096 g/micron | 129.4 g/mil | ISO 6383/2 |
| Dart Drop Test | 140 g | 0.309 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 26.0 MPa | 3770 psi | |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | 22mm/min; ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | ISO 11357-3 |
| Vicat Softening Point | 96.0 °C | 205 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 190 °C | 320 - 374 °F |
Users viewing this material also viewed the following:
- DSM Akulon® S223-E Nylon 66 (European and Asian Grade) (Dry) (discontinued **)
- Lucent Polymers TPO-30T Thermoplastic Polyolefin, 30% Mineral Filled
- Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
- Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed
- Michelman® Licomer® M 55 Styrene-Acrylate copolymer dispersion
- SABIC Innovative Plastics LNP STAT-KON DE0039 PC
- Chase Plastics CP Pryme® NN100L (COND, 50% RH) Nylon 66, Internally Lubricated
- UBE UBESTA® 3030U Nylon 12 (After Hexane for 500 hours)
- Arlon 44576XB015 0.015" (0.381 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate
- 3M Scotch-Weld™ SI1500 Surface Insensitive Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved