SABIC HP0722N Low Density Polyethylene for Blown Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | SABIC |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC HP0722N Low Density Polyethylene for Blown Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: HP0722N is a Low Density Polyethylene grade suitable for producing medium duty films and contains no slip or antiblock additives. It yields good toughness and optical properties in the film.Typical Applications: HP0722N can be used for medium duty bags, shrink films, shopping bags, lamination films and frozen food packaging.Information provided by SABIC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Flow | 0.75 g/10 min @Load 21.6 kg, Temperature 190 °C |
0.75 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 280 g | 280 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.00 g/micron | 178 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.60 g/micron | 142 g/mil | ASTM D1922 |
| Dart Drop | 4.00 g/micron | 102 g/mil | ASTM D1709 |
| Dart Drop Test | 200 g | 0.441 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 200 MPa | 29000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 60 % | 60 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 170 - 185 °C | 338 - 365 °F | |
| Blow-up Ratio (BUR) | 2.5 - 4.0 | 2.5 - 4.0 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 GF 30 002 TS PA6 reinforced with glass fiber, heat stabilized
- PolyOne Geon™ L4605 Green 5765 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
- NIZHNEKAMSKNEFTEKHIM PE 4431S (30405) Linear Low Density Polyethylene
- Lubriplate FMO 85 AW USP Mineral Oil-Based Food Machinery Grade Oil
- Karina E 650D48/1 Black PVC Compound
- Latrobe CBS-50â„¢ NiL VIM-VAR High Performance Carburizing Bearing and Gear Steel
- A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene
- Formosa Plastics Formolene® 6501A Blow Molding and Injection Molding Polypropylene
- Adamas Adalon® 301 PTFE, 10% Graphite
- Ametek Tungsten-Copper Composites AWC 8020
Copyright © lookpolymers.com All Rights Reserved