NOVA Chemicals Sclair® 19H Homopolymer HDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 19H Homopolymer HDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: High stiffnessGood processability Low gel Applications: BlendingCo-extrusionInformation provided by Nova Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Water Vapor Transmission | 4.20 g/m²/day | 0.270 g/100 in²/day | |
| Oxygen Transmission Rate | 1705 cc/m²/day | 109.8 cc/100 in²/day | |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.38 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 26.0 MPa | 3770 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| Puncture Energy | 1.14 J | 0.841 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 18 g | 18 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1800 g | 1800 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 53.0 MPa | 7690 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| 1% Secant Modulus, MD | 829.99 MPa | 120380 psi | ASTM D882 |
| 1% Secant Modulus, TD | 1330 MPa | 192900 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 81 % | 81 % | ASTM D1003 |
| Gloss | 5.0 % | 5.0 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® ABS 440 Injection Molding Grade
- Taiwan PU Corporation TPUI-E98 General Grade, Injection Molding Polyester Base TPU
- Stir SpA SR 78 REF CZ (PVC)
- A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene
- Hexcel® HexPly® EH 84 120°C Curing Epoxy Matrix, High Modulus 12k carbon UD tape 110 g/m2
- Dow Corning SILASTIC® 25786-V SILICONE RUBBER RED
- DuPont™ Bynel® 41E871 Anhydride Modified LLDPE
- Bhansali Engineering Abstron KU602 ABS Heat Resistant
- LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved