NOVA Chemicals Sclair® 19G Homopolymer HDPE Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | NOVA Chemicals |
| Trade Name | Sclair® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Sclair® 19G Homopolymer HDPE Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Excellent barrier propertiesHigh stiffnessGood processability Low gel Applications: Barrier filmsCo-extrusionDry food packagingInformation provided by Nova Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Water Vapor Transmission | 2.79 g/m²/day | 0.180 g/100 in²/day | |
| Oxygen Transmission Rate | 1628 cc/m²/day | 104.8 cc/100 in²/day | |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| Puncture Energy | 0.722 J | 0.533 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 24 g | 24 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 450 g | 450 g | ASTM D1922 |
| Dart Drop Test | 29.0 g | 0.0639 lb | F<sub>50</sub>; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM D882 |
| 1% Secant Modulus, MD | 839.99 MPa | 121830 psi | ASTM D882 |
| 1% Secant Modulus, TD | 1270 MPa | 184200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 41 % | 41 % | ASTM D1003 |
| Gloss | 14 % | 14 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Enviramid™ N1300HL BK/UV2 Post Consumer Recycle Nylon 66
- ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder (discontinued **)
- Solvay TECHNYL® eXten D238 V30 Nylon 6,10, 30% glass fiber, Conditioned
- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 30% Cold Work
- Chosun Refractories GM-1 Special Mortar
- Abatron AboWeld 8201-14/AboCure 8201-14 Carbon-Filled Electrically Conductive Epoxy Compound
- BASF Ultramid® 8231G HS 14% Glass Filled PA6 (Conditioned)
- Murtfeldt Murpec® SP Polyetheretherketone
- Hexion Bakelite™ EP 8412 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage
Copyright © lookpolymers.com All Rights Reserved