NOVA Chemicals Novapol® PF-0318-E Butene LLDPE Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer	NOVA Chemicals
Trade Name	Novapol®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NOVA Chemicals Novapol® PF-0318-E Butene LLDPE Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PF-0318-E complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. It is also biologically and chemically inert.Features: Excellent optical properties, Easy processabilityAdditives: High temperature AOApplications: Cast Stretch WrapFilm properties are Typical of cast film extruded at 280°C.

Physical Properties	Metric	English	Comments
Density	0.919 g/cc	0.0332 lb/in³	ASTM D 792
Thickness	20.0 microns	0.787 mil
Melt Flow	2.3 g/10 min @Load 2.16 kg, Temperature 190 °C	2.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.00 MPa	1310 psi	ASTM D 882
Film Tensile Strength at Yield, TD	9.00 MPa	1310 psi	ASTM D 882
Film Elongation at Break, MD	498 %	498 %	ASTM D 882
Film Elongation at Break, TD	775 %	775 %	ASTM D 882
Elmendorf Tear Strength MD	63 g	63 g	ASTM D 1922
Elmendorf Tear Strength TD	350 g	350 g	ASTM D 1922
Elmendorf Tear Strength, MD	3.15 g/micron	80.0 g/mil	ASTM D 1922
Elmendorf Tear Strength, TD	17.5 g/micron	445 g/mil	ASTM D 1922
Film Tensile Strength at Break, MD	36.0 MPa	5220 psi	ASTM D 882
Film Tensile Strength at Break, TD	23.0 MPa	3340 psi	ASTM D 882
1% Secant Modulus, MD	156 MPa	22600 psi	ASTM D 882
1% Secant Modulus, TD	177 MPa	25700 psi	ASTM D 882

Optical Properties	Metric	English	Comments
Haze	1.3 %	1.3 %	ASTM D 1003
Gloss	91 %	91 %	45°; ASTM D 2457

Descriptive Properties	Value	Comments
Low Friction Puncture	9 (ft-lb/mil)	NOVA Chemicals test method

Users viewing this material also viewed the following: