- Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
- Ineos ABS Lustran® SAN GF30 Glass Fiber Reinforced
Ineos ABS Lustran® SAN GF30 Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® SAN GF30 Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in | Test Condition: 150x105x3; acc. ISO 2577 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Break | 1.2 % | 1.2 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 180 MPa | 26100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | 2 mm/min; ISO 178 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | ISO 75-1,-2 |
| Vicat Softening Point | 109 °C @Load 5.10 kg |
228 °F @Load 11.2 lb |
50°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® SLX1231D PC Copolymer (Asia Pacific)
- DuPont Performance Polymers Delrin® 300TE BK602 Acetal Homopolymer (Unverified Data**)
- Lucite International Lucite® 41 Acrylic Resin for Casting and Embedments
- Solvay Specialty Polymers Halar® 9414 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE), Filled
- Solvay Specialty Polymers Omnix® 4050 Polyamide, High Performance (HPPA) (Conditioned)
- A. Schulman PP 3482-01 Polypropylene Nucleated Homopolymer Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Non-Black Peroxide Cure
- ExxonMobil Paxon™ AD60-005 Blow Molding Resin
- Arlon R30370A008 0.008" Uncured Silicone Rubber with Fiberglass Substrate
- Asahi Kasei Tenac® LS701 Homopolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved