LNP Lubricomp® QFL-4036 BK8-115 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant  (disconti

Category Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® QFL-4036 BK8-115 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement, PTFE Lubricant  (disconti.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
Method A; ASTM D792
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Water Absorption 0.10 %
0.10 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0080 cm/cm
0.0070 - 0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 149 MPa
21600 psi
ASTM D638
Tensile Strength, Yield 149 MPa
21600 psi
ASTM D638
Elongation at Break 2.6 %
2.6 %
ASTM D638
Elongation at Yield 2.6 %
2.6 %
ASTM D638
Tensile Modulus 11.0 GPa
1600 ksi
ASTM D638
Flexural Strength 221 MPa
32100 psi
ASTM D790
Flexural Modulus 8.48 GPa
1230 ksi
ASTM D790
Izod Impact, Notched 1.17 J/cm

@Thickness 3.18 mm
2.19 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 9.39 J/cm

@Thickness 3.18 mm
17.6 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 65.0 kJ/m²
30.9 ft-lb/in²
ISO 180
Falling Dart Impact 8.50 J
6.27 ft-lb
ASTM D3763
Impact Test 3.19 J
2.35 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic 0.71
0.71
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.52
0.52
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 30.2 x 10-8 mm³/N-M
15.0 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 224 °C
435 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 216 °C
421 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 268 - 274 °C
514 - 525 °F
Mold Temperature 82.2 - 93.3 °C
180 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.20 %
0.20 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi
Descriptive Properties Value Comments
Color Black