BASF Ultramid® N-333 NF3001 33% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® N-333 NF3001 33% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid N-333 NF3001 is a 33% glass reinforced, heat stabilized, injection molding
PA66 uncolored.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Water Absorption | 5.7 % | 5.7 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 23°C/50% R.H.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 195 MPa | 28300 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 9.60 GPa | 1390 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO Test |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | 10 K/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Suprex Clay Filler
- Silberline Silvet® 960-20-P
- Teknor Apex Flexalloy® 3500-75NT Polyvinyl Chloride Elastomer
- DuPont Elvax® 760 Ethylene Vinyl Acetate
- Westlake Plastics Norylux™ Modified Polyphenylene Oxide 30% glass filled
- Toyobo GLAMIDE® T-402 Nylon-6
- Epoxyset Epoxiohm EO-30FST Electrically Conductive Epoxy Adhesive
- 3M Scotch® 231 Performance Masking Tape
- 3M Scotchcal™ ElectroCut™ 7725-24 Graphic Film
- DuPont Performance Polymers Crastin® HR5330HF NC010 PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved