Stratasys® ABS-M30i
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Stratasys |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stratasys® ABS-M30i.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS-M30i is a high strength material well suited for the medical, pharmaceutical
and food packaging industries. Parts manufactured with ABS-M30i material
are biocompatible (ISO 10993 certified) and can be gamma or EtO sterilized.
When combined with Fortus 3D Production Systems, ABS-M30i gives you
biocompatible Real Partsâ„¢ with excellent mechanical properties that are well
suited for conceptual modeling, functional prototyping, manufacturing tools,
and end-use-parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109.5 | 109.5 | ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 52 % | 52 % | flexural; ASTM D790 |
| Elongation at Yield | 4 % | 4 % | ASTM D638 |
| Tensile Modulus | 2.413 GPa | 350.0 ksi | ASTM D638 |
| Flexural Strength | 61 MPa | 8800 psi | ASTM D790 |
| Flexural Modulus | 2.317 GPa | 336.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm | 2.60 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 88.2 µm/m-°C @Temperature -40.0 - 37.8 °C |
49.0 µin/in-°F @Temperature -40.0 - 100 °F |
ASTM E831 |
| CTE, linear, Transverse to Flow | 84.6 µm/m-°C @Temperature -40.0 - 37.8 °C |
47.0 µin/in-°F @Temperature -40.0 - 100 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Glass Transition Temp, Tg | 108 °C | 226 °F | DSC |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | IEC 60112 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N 3330 Acrylonitrile-Butadiene Rubber
- Solvay Engineered Polymers SEQUEL® 5220 Engineered Polyolefin (discontinued **)
- Kraton® D1186 B (SBS) Branched Triblock Copolymer
- LG Chemical LUPOY GN5007FL PC/ABS, Halogen Free Flame Retardant, Heat Resistance
- A. Schulman FORMION™ FI 391E Ionomer
- ExxonMobil 20W-50 Exxon Aviation Oil
- Washington Penn PPH4CF2.5 Polypropylene, 25% Calcium Carbonate Filled
- Total Lumicene® MR10MX0 Metallocene Random Copolymer Polypropylene, Injection Molding and Injection Blow Molding
- ChevronTexaco Syntholube® ISO 32 Compressor Oil
- NOVA Chemicals Sclair® 35BPM MDPE Extrusion Resin, 2.2% Carbon Black Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved