Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Cycoloy® C3650 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according .. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection mol.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® FXD9945A PC (Asia Pacific) UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® LUX9130T PC COPOLYMER (Asia Pacific) LUX9130T Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm / 5VA rating at 6.0mm and is U.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | ASTM D638 |
SABIC Innovative Plastics LNP COLORCOMP D1000FH PC (Asia Pacific) LNP COLORCOMP* D1000FH is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Low Extractible. |
|||
Tensile Strength, Yield | 64.0 - 155 MPa | 9280 - 22500 psi | Average value: 100 MPa Grade Count:6 |
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | ASTM D638 |
Covestro Apec® DP9-9331 High-Heat Polycarbonate, General Purpose
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DD0009P PC (Asia Pacific) LNP STAT-KON* DD0009P is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DD0009PC PC (Europe-Africa-Middle East) LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP MFB63 PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MFB63 is a compound based on Polypropylene resin containing Glass Bead, Glass Fiber. |
|||
Tensile Strength, Yield | 64.0 MPa @Temperature -40.0 °C |
9280 psi @Temperature -40.0 °F |
ISO Data |
Styrolution Terblend® N NM-11 ABS/PA6 (Dry) Terblend N NM-11 is an ABS/PA6 blend combining very high impact strength, even at low temperatures, with an excellent processability and surface appearance.Information provided by STYROLUTION, which.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Asia Pacific) Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Europe-Africa-Middle East) Noryl* LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Europe-Africa-Middle East) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON 9X02785 PC LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL FXN121LG PPE+HIPS (Asia Pacific) Noryl* FXN121LG is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this r.. |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | ASTM D638 |
Aclo Accucomp Polycarbonate POL050L Low Viscosity |
|||
Tensile Strength, Yield | 64.0 MPa | 9280 psi | 2 in/min; ASTM Test |
BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Dry) Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing c.. |