SABIC Innovative Plastics LNP STAT-KON DD0009PC PC (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON DD0009PC PC (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.

Physical Properties	Metric	English	Comments
Density	1.29 g/cc	0.0466 lb/inÂ³	ASTM D792
Moisture Absorption	0.130 %	0.130 %	50% RH, 24 hrs; ASTM D570
	0.230 %	0.230 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0078 cm/cm @Time 86400 sec	0.0078 in/in @Time 24.0 hour	ISO 294
	0.0080 cm/cm @Time 86400 sec	0.0080 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0080 cm/cm @Time 86400 sec	0.0080 in/in @Time 24.0 hour	ASTM D955
	0.0080 cm/cm @Time 86400 sec	0.0080 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	53.0 MPa	7690 psi	ISO 527
	54.0 MPa	7830 psi	ASTM D638
Tensile Strength, Yield	59.0 MPa	8560 psi	ISO 527
	64.0 MPa	9280 psi	ASTM D638
Elongation at Break	9.5 %	9.5 %	ISO 527
	10 %	10 %	ASTM D638
Elongation at Yield	4.4 %	4.4 %	ISO 527
	4.8 %	4.8 %	ASTM D638
Tensile Modulus	2.62 GPa	380 ksi	50 mm/min; ASTM D638
	2.80 GPa	406 ksi	1 mm/min; ISO 527
Flexural Strength	102 MPa	14800 psi	ASTM D790
	102 MPa	14800 psi	ISO 178
Flexural Modulus	2.82 GPa	409 ksi	ASTM D790
	3.00 GPa	435 ksi	ISO 178
Izod Impact, Notched	1.14 J/cm	2.14 ft-lb/in	ASTM D256
Izod Impact, Unnotched	20.93 J/cm	39.21 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	9.00 kJ/mÂ²	4.28 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	134 kJ/mÂ²	63.8 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	12.0 J	8.85 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	35.0 J	25.8 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	140 Â°C @Thickness 3.20 mm	284 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	128 Â°C	262 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	130 Â°C @Thickness 3.20 mm	266 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Flammability, UL94	V-1 @Thickness 1.50 mm	V-1 @Thickness 0.0591 in	UL 94 by SABIC-IP

Electrical Properties	Metric	English	Comments
Surface Resistance	100 - 1.00e+6 ohm	100 - 1.00e+6 ohm	ASTM D257