SABIC Innovative Plastics LNP THERMOCOMP MFB63 PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MFB63 PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MFB63 is a compound based on Polypropylene resin containing Glass Bead, Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 3.3 % | 3.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.40 GPa | 783 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.90 GPa | 711 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 112 µm/m-°C @Temperature 23.0 - 60.0 °C |
62.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 HS-GV35 Nylon 6.6 for injection molding, 35% glass fiber reinforced
- Parker Chomerics PREMIER™ A230-FRHF EMI Shielding Plastic
- Chevron Phillips HiD® 9605D HDPE Cast Film Resin (discontinued **)
- Pau Tai UNISTAB MS-130 Solid Complex Stabilizer
- Manufacturing Insight EFR-1FM Enhanced Fire Retardant Additive
- Lucite International Colacryl ® TS2082 Acrylic Resin
- SABIC Innovative Plastics LNP THERMOCOMP AF001H ABS (Asia Pacific)
- China-Yixing Longly Refractories ASM-125 Cordierite-Mullite
- 3M SJ5500 Protective Product, Molded Shapes
- Polyram Polytron P50B01 Homopolymer Polypropylene, Chemically Coupled 50% LGF
Copyright © lookpolymers.com All Rights Reserved