BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® HPN 9362 40% Mineral Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid HPN 9362 is a 40% mineral reinforced, impact modified nylon 6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing cycle time. It possesses excellent balance of strength, stiffness and toughness combined with a high level of drop weight impact, excellent processability and chemical resistance to greases, oils and hydrocarbons.

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³	ISO 1183
Water Absorption	4.9 %	4.9 %	ISO 62
Moisture Absorption at Equilibrium	1.4 %	1.4 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.010 cm/cm	0.010 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	119	119	ASTM Test
Tensile Strength at Break	62.0 MPa	8990 psi	0.2 in/min; ASTM Test
Tensile Strength, Yield	64.0 MPa	9280 psi	2 in/min; ASTM Test
	65.0 MPa	9430 psi	50mm/min; ISO 527
Elongation at Break	15 %	15 %	50mm/min, Nominal strain; ISO 527
	15 %	15 %	2 in/min; ASTM Test
	15 %	15 %	0.2 in/min; ASTM Test
Elongation at Yield	3.0 %	3.0 %	50mm/min; ISO 527
	3.0 %	3.0 %	2 in/min; ASTM Test
Tensile Modulus	4.33 GPa	628 ksi	1mm/min; ISO 527
Flexural Strength	109 MPa	15800 psi	ASTM Test
	30.0 MPa @Temperature 120 °C	4350 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 93.0 °C	4350 psi @Temperature 199 °F	ASTM Test
	45.0 MPa @Temperature 65.0 °C	6530 psi @Temperature 149 °F	ASTM Test
	180 MPa @Temperature -40.0 °C	26100 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	4.00 GPa	580 ksi	ASTM Test
	0.750 GPa @Temperature 120 °C	109 ksi @Temperature 248 °F	ASTM Test
	0.770 GPa @Temperature 93.0 °C	112 ksi @Temperature 199 °F	ASTM Test
	1.25 GPa @Temperature 65.0 °C	181 ksi @Temperature 149 °F	ASTM Test
Izod Impact, Notched	0.860 J/cm @Thickness 3.17 mm	1.61 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179
	0.300 J/cm² @Temperature -30.0 °C	1.43 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	23.0 µm/m-°C @Temperature -30.0 - 30.0 °C	12.8 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F	ASTM Test
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	95.0 °C	203 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	Yes
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes