- Polymer Property : Tensile Strength, Yield = 5220 psi
Polymer Property : Tensile Strength, Yield = 5220 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| SABIC PP 578P Polypropylene Homopolymer for Injection Molding Product Description: PP 578P is a controlled rheology PP grade of medium molecular weight distribution suitable for injection molding applications. It gives consistent processability, good flow pr.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | Type I, 5.1 mm/min; ASTM D638 |
| PolyOne Geon™ HTX Ultra LA436G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy) Higher gloss, wider processing window version of Geon HTX Ultra LA426G.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA436G Black 2880... |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Ineos Nova 4214 Medium Impact Polystyrene
(discontinued **) Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless o.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Ineos ABS Lustran® QE 1094 AS General Purpose, High-Impact
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with La.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | |
| Ineos ABS Lustran® QE 1006, Extrusion Grade
(discontinued **) Extrusion grade with high impact.Applications: High impact plates.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majo.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50mm/min; ASTM D638 |
| Reliance Industries Repol H029SG Polypropylene REPOL Polypropylene H029SG is being manufactured using Unipol PP process, which combines the production efficiency of gas phase fluidized bed reactor with the high activity stereospecific catalyst s.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50mm/min; ASTM D638 |
| Reliance Industries Repol H050MN Polypropylene REPOL Polypropylene H050MN is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min |
| Eastman Tenite 358-10 Cellulose Acetate Propionate
(discontinued **) 10% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Flint Hills P4G2T-077D Homopolymer Polypropylene Homopolymer, FDA compliantFeatures: Antistat.Applications: Extrusion: straw grade.Former Huntsman polypropylene products are now produced by Flint Hills Resources. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Flint Hills P4G4T-017A Homopolymer Polypropylene Homopolymer, and FDA compliant.Features: Highly lubricated and antistat.Applications: Injection molding: closures.Former Huntsman polypropylene products are now produced by Flint Hills Resources. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Flint Hills P5L2K-055 Polypropylene Random Copolymer Features: Excellent clarity. Product does not contain animal derived components. Phthalate-free.Applications: Injection molding: extrusion blow molding, injection blow molding, stretch blow moldin.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| IRPC Polimaxx Polene 1100RC Polypropylene Homopolymer CHARACTERISTICS: HIGH FLOW, GOOD STIFFNESS, GOOD PROCESSABILITY, GOOD MELT STABILITYAPPLICATIONS: INJECTION MOLDING FOR THIN WALL PARTS, HOUSE WARES EXTRUSION COATING FOR COATED WOVEN BAGS AND TARPA.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| IRPC Polimaxx Polene 1125NA Polypropylene Homopolymer CHARACTERISTICS: GOOD EXTRUDABILITY, LOW GEL CONTAIN MEDIUM SLIP AND ANTIBLOCK ADDITIVESAPPLICATIONS: CAST FILM AND TUBULAR BLOW FILM WATER QUENCH CPP FILM FOR FOOD PACKAGING, CPP FILM FOR LAMINATIO.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DZL24 PC LNP LUBRICOMP* DZL24 is a compound based on Polycarbonate resin containing 20% Milled Glass, 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP SABIC® PPcompound 19T1020 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO 527 |
| SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 2 in/min; ASTM Test |
| Styrolution Terblend® N NM-12 ABS/PA6 (Conditioned) Terblend N NM-12 is an ABS/PA6 blend combining high impact strength and rigidity with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| UBE UMERIT 2000F Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1006 is a 20% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1006S is a 20% talc filled homopolymer polypropylene compound formulated with an internal mold release. Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1006 is a 20% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ASTM D638 |
| A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene DescriptionPolypropylene PP 3369-01 is a medium-flow homopolymer polypropylene nucleated and anti-static designed for the molding of thin walled, and large parts.ApplicationTypical applications of P.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1006 is a 20% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-709S ABS - Extrusion Super Impact Extrusion |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Crastin® ST820 BK503 Polybutylene Terephthalate (PBT)
(Unverified Data**) Unreinforced Polybutylene Terephthalate with Excellent Impact Resistance Crastin ST820 BK503 is an unreinforced Super Tough black polybutylene terephthalate resin for injection molding.Information p.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO R527 |
| Arkema Group Orgalloy® LE 60 SF Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0334T10L Talc Reinforced |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 2 in/min; ASTM Test |
| BASF Ultramid® 8202 HS BK-102 PA6 (Conditioned) Ultramid 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses .. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO R527 |
| Fainplast Compounds RE 236 Rigid PVC, Extrusion Electric channels |
|||