Eastman Tenite 358-10 Cellulose Acetate Propionate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Eastman Tenite 358-10 Cellulose Acetate Propionate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm <br>@Thickness 3.20 mm |
0.0020 - 0.0060 in/in <br>@Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min |
| Elongation at Break | 36 % | 36 % | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Tensile Modulus | 1.66 GPa | 241 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB <br>@Temperature -30.0 °C |
NB <br>@Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.82 J/cm² | 8.66 ft-lb/in² | |
| 0.850 J/cm² <br>@Temperature -30.0 °C |
4.05 ft-lb/in² <br>@Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.0 µm/m-°C <br>@Temperature 20.0 °C |
48.9 µin/in-°F <br>@Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 140 µm/m-°C <br>@Temperature 20.0 °C |
77.8 µin/in-°F <br>@Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | |
| Vicat Softening Point | 91.0 °C | 196 °F | |
| Glass Transition Temp, Tg | 104 °C | 219 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 240 °C | 446 - 464 °F |
Users viewing this material also viewed the following:
- Polymer Resources PPX-GP3 Modified-PPO, General Purpose
- NOVA Chemicals Surpass® HPs900-C Octene sLLDPE Film Resin
- Solvay TECHNYL® A 60 G1 V25 PA66, 25% glass fiber, Conditioned
- A. Schulman POLYBATCH™ ABPP-05 Antiblock Concentrate
- DSM Akulon® S223-HM8 (Dry) 40% Mineral Reinforced, Heat Stabilized Nylon 66 (North America)
- 3M 7660-S-HSG Cold Shrink QT-III Silicone Rubber Skirted Termination Kits
- PolyOne Synprene® IT 36-021 NATURAL Thermoplastic Elastomer - SBC (discontinued **)
- A. Schulman FORMION™ FI 388 Ionomer
Copyright © lookpolymers.com All Rights Reserved